Muna amfani da kukis don inganta ƙwarewar ku.Ta ci gaba da bincika wannan rukunin yanar gizon, kun yarda da amfani da kukis.Ƙarin Bayani.
Tsaftataccen tsarin magungunan tururi ko tsantsa sun haɗa da janareta, bawul masu sarrafawa, bututun rarraba ko bututun, ma'aunin zafi ko ma'aunin zafi, ma'aunin matsi, masu rage matsa lamba, bawul ɗin aminci, da tarawa mai ƙarfi.
Yawancin waɗannan sassa an yi su ne da bakin karfe 316 L kuma suna ɗauke da gaskets na fluoropolymer (yawanci polytetrafluoroethylene, wanda kuma aka sani da Teflon ko PTFE), da Semi-karfe ko wasu kayan elastomeric.
Waɗannan abubuwan haɗin gwiwar suna da saurin lalacewa ko lalacewa yayin amfani, wanda ke shafar ingancin ƙaƙƙarfan kayan aikin Tsabtace Tsabtace Steam (CS).Aikin dalla-dalla a cikin wannan labarin ya kimanta samfuran bakin karfe daga nazarin shari'ar tsarin CS guda huɗu, an kimanta haɗarin yuwuwar tasirin lalata akan tsari da tsarin injiniya mai mahimmanci, kuma an gwada ɓarna da ƙarfe a cikin condensate.
Ana sanya samfurori na ɓarna bututu da sassan tsarin rarraba don bincika samfuran lalata.9 Ga kowane takamaiman yanayi, an kimanta yanayin saman daban-daban.Misali, daidaitaccen blush da tasirin lalata an kimanta su.
An yi la'akari da filaye na samfurorin ƙididdiga don kasancewar ɓangarorin blush ta amfani da dubawa na gani, Auger electron spectroscopy (AES), electron spectroscopy for chemical analysis (ESCA), scanning electron microscopy (SEM) da kuma X-ray photoelectron spectroscopy (XPS).
Waɗannan hanyoyin za su iya bayyana kaddarorin jiki da na atomic na lalata da adibas, da kuma tantance mahimman abubuwan da ke shafar kaddarorin ruwan fasaha ko samfuran ƙarshe.daya
Abubuwan lalata na bakin karfe na iya ɗaukar nau'ikan nau'ikan nau'ikan nau'ikan nau'ikan nau'ikan nau'ikan nau'ikan nau'ikan nau'ikan nau'ikan nau'ikan nau'ikan nau'ikan nau'ikan nau'ikan nau'ikan nau'ikan nau'ikan nau'ikan nau'ikan nau'ikan nau'ikan nau'ikan nau'ikan nau'ikan nau'ikan nau'ikan nau'ikan nau'ikan nau'ikan nau'ikan nau'ikan nau'ikan nau'ikan nau'ikan nau'ikan nau'ikan nau'ikan nau'ikan nau'ikan nau'ikan nau'ikan nau'ikan nau'ikan nau'ikan nau'ikan nau'ikan nau'ikan nau'ikan nau'ikan nau'ikan nau'ikan nau'ikan lalata kamar nau'in nau'in nau'in nau'in nau'in nau'in nau'in nau'in nau'in nau'in nau'in nau'in nau'in nau'in nau'in nau'in nau'in nau'in nau'in nau'in nau'in nau'in nau'in nau'in nau'in nau`in) na iya daukar nau’in nau’i irin su carmine Layer na iron oxide (brown ko ja) a saman kasa ko sama da Layer na iron oxide (baki ko launin toka)2.Ikon ƙaura zuwa ƙasa.
Ƙarfe oxide Layer (black blush) na iya yin kauri na tsawon lokaci yayin da adibas ɗin ke ƙara fitowa fili, kamar yadda ake nunawa ta barbashi ko adibas da ake iya gani a saman ɗakin da ake yin haifuwa da kayan aiki ko kwantena bayan haifuwar tururi, akwai ƙaura.Binciken dakin gwaje-gwaje na samfuran condensate ya nuna yanayin tarwatsewar sludge da adadin karafa masu narkewa a cikin ruwan CS.hudu
Kodayake akwai dalilai da yawa na wannan al'amari, janareta na CS yawanci shine babban mai ba da gudummawa.Ba sabon abu ba ne don samun jan ƙarfe oxide (launin ruwan kasa / ja) akan saman da baƙin ƙarfe oxide (baƙar fata / launin toka) a cikin iska wanda ke yin ƙaura a hankali ta hanyar tsarin rarraba CS.6
Tsarin rarraba CS shine saitin reshe tare da wuraren amfani da yawa yana ƙarewa a wurare masu nisa ko a ƙarshen babban taken da manyan kantunan reshe daban-daban.Tsarin na iya haɗawa da adadin masu sarrafawa don taimakawa fara matsa lamba / rage yawan zafin jiki a takamaiman wuraren amfani waɗanda zasu iya zama maƙasudin lalata.
Hakanan lalata na iya faruwa a cikin tarkon ƙira mai tsafta waɗanda aka sanya a wurare daban-daban a cikin tsarin don cire condensate da iska daga tururi mai tsafta ta cikin tarko, bututun bututun da ke ƙasa ko fitar da bututun kodensate.
A mafi yawan lokuta, ƙaura mai yuwuwa ne inda tsatsa ta taru akan tarko kuma ta girma zuwa cikin bututun da ke kusa da su ko kuma masu tara abubuwan amfani;tsatsa da ke tasowa a cikin tarko ko wasu abubuwan da za a iya gani a sama daga tushen tare da ƙaura akai-akai a ƙasa da sama.
Wasu sassa na bakin karfe kuma suna nuna matsakaicin matsakaici zuwa manyan matakan sifofin ƙarfe, gami da delta ferrite.An yi imanin cewa lu'ulu'u na Ferrite suna rage juriya na lalata, kodayake suna iya kasancewa a cikin kaɗan kamar 1-5%.
Ferrite kuma baya da juriya ga lalata kamar tsarin kristal austenitic, don haka zai fi dacewa lalata.Za a iya gano ferrite daidai tare da bincike na ferrite da daidai-daidai tare da maganadisu, amma akwai iyakoki masu mahimmanci.
Daga saitin tsarin, ta hanyar ƙaddamarwa na farko, da farawa na sabon janareta na CS da bututun rarraba, akwai abubuwa da yawa waɗanda ke taimakawa ga lalata:
A tsawon lokaci, abubuwa masu lalata irin waɗannan na iya samar da samfuran lalata lokacin da suka hadu, haɗuwa, da haɗuwa da gaurayawan ƙarfe da ƙarfe.Baƙar fata yawanci ana ganin farko a cikin janareta, sannan yana bayyana a cikin bututun fitar da janareta kuma daga ƙarshe a cikin tsarin rarraba CS.
An gudanar da bincike na SEM don bayyana microstructure na samfurori na lalata da ke rufe dukkan farfajiya tare da lu'ulu'u da sauran barbashi.A baya ko m surface a kan abin da barbashi aka samu bambanta daga daban-daban maki na baƙin ƙarfe (Fig. 1-3) zuwa na kowa samfurori, wato silica / baƙin ƙarfe, yashi, vitreous, kama adibas (Fig. 4).Har ila yau, an yi nazarin tarkon tarkon tururi (Fig. 5-6).
Gwajin AES hanya ce ta nazari da ake amfani da ita don tantance sinadarai na bakin karfe da tantance juriyar lalatarsa.Har ila yau yana nuna lalacewar fim ɗin da ba a so ba da kuma raguwa a cikin tattarawar chromium a cikin fim ɗin da ba a so ba yayin da saman ya lalace saboda lalata.
Don siffanta nau'ikan nau'ikan saman kowane samfurin, an yi amfani da sikanin AES (bayanin martaba na abubuwan da ke sama sama da zurfin).
Kowane rukunin yanar gizon da aka yi amfani da shi don nazarin SEM da haɓaka an zaɓi su a hankali don samar da bayanai daga yankuna na yau da kullun.Kowane binciken ya ba da bayanai daga saman ɗigon ƙwayoyin ƙwayoyin cuta (ƙimantawa a 10 angstroms [Å] a kowane Layer) zuwa zurfin ƙarfe na ƙarfe (200-1000 Å).
An yi rikodin adadi mai yawa na baƙin ƙarfe (Fe), chromium (Cr), nickel (Ni), oxygen (O) da carbon (C) a duk yankuna na Rouge.An bayyana bayanan AES da sakamakon a cikin sashin binciken shari'ar.
Sakamakon AES gabaɗaya don yanayin farko ya nuna cewa iskar oxygen mai ƙarfi yana faruwa akan samfuran tare da babban adadin Fe da O (iron oxides) da ƙarancin abun ciki na Cr a saman.Wannan ajiya mai ja yana haifar da sakin barbashi waɗanda zasu iya gurɓata samfurin da filaye a cikin hulɗa da samfurin.
Bayan da aka cire blush, samfurori na "passivated" sun nuna cikakkiyar farfadowa na fim din da ba a so ba, tare da Cr ya kai matakan maida hankali fiye da Fe, tare da Cr: Fe surface rabo daga 1.0 zuwa 2.0 da kuma rashin ƙarfe oxide gaba ɗaya.
An bincika wurare daban-daban ta hanyar amfani da XPS/ESCA don kwatanta matakan farko da jihohin oxidation na Fe, Cr, sulfur (S), calcium (Ca), sodium (Na), phosphorus (P), nitrogen (N), da O. da C (tebur A).
Akwai bayyanannen bambanci a cikin abun ciki na Cr daga dabi'u kusa da Layer passivation zuwa ƙananan dabi'u yawanci ana samun su a cikin allo.Matakan baƙin ƙarfe da chromium da aka samo a saman suna wakiltar kauri daban-daban da maki na adibas rouge.Gwaje-gwajen XPS sun nuna haɓaka a Na, C ko Ca akan filaye masu ƙazanta idan aka kwatanta da tsabtacewa da wuraren da ba a so.
Gwajin XPS kuma ya nuna babban matakan C a cikin jan ƙarfe (baƙar fata) ja da kuma Fe (x) O (y) (iron oxide) a ja.Bayanan XPS ba su da amfani don fahimtar canje-canjen saman yayin lalata saboda yana kimanta duka jan ƙarfe da ƙarfe na tushe.Ana buƙatar ƙarin gwajin XPS tare da samfurori mafi girma don kimanta sakamako da kyau.
Mawallafa na baya kuma sun sami matsala wajen kimanta bayanan XPS.10 Binciken filin yayin aikin cirewa ya nuna cewa abun cikin carbon yana da girma kuma yawanci ana cire shi ta hanyar tacewa yayin aiki.SEM micrographs da aka ɗauka kafin da kuma bayan maganin kawar da wrinkle suna kwatanta lalacewar saman da waɗannan adibas suka haifar, gami da pitting da porosity, waɗanda ke shafar lalata kai tsaye.
Sakamakon XPS bayan wucewa ya nuna cewa rabon abun ciki na Cr: Fe akan saman ya kasance mafi girma lokacin da aka sake yin fim ɗin wucewa, ta yadda za a rage yawan lalata da sauran mummunan tasiri a saman.
Samfuran coupon sun nuna haɓaka mai girma a cikin rabon Cr: Fe tsakanin “kamar yadda yake” saman da saman da ke wucewa.An gwada ma'auni na farko na Cr: Fe a cikin kewayon 0.6 zuwa 1.0, yayin da ƙimar wucewar magani bayan jiyya ya kasance daga 1.0 zuwa 2.5.Ma'auni don electropolished da passivated bakin karfe suna tsakanin 1.5 da 2.5.
A cikin samfurorin da aka yi wa bayan aiki, matsakaicin zurfin Cr: Fe (wanda aka kafa ta amfani da AES) ya kasance daga 3 zuwa 16 Å.Suna kwatanta da kyau da bayanai daga binciken da Coleman2 da Roll suka buga a baya.9 Filayen duk samfurori suna da matakan daidaitattun matakan Fe, Ni, O, Cr, da C. Ƙananan matakan P, Cl, S, N, Ca, da Na an samo su a yawancin samfurori.
Waɗannan abubuwan da suka saura sun zama na yau da kullun na masu tsabtace sinadarai, tsaftataccen ruwa, ko gogewar lantarki.Bayan ƙarin bincike, an sami wasu gurɓataccen silicon a saman kuma a matakai daban-daban na kristal austenite kanta.Tushen ya bayyana shine abun ciki na silica na ruwa/ tururi, goge goge, ko narkar da gilashin gani a cikin tantanin halitta na CS.
An ba da rahoton samfuran lalata da aka samu a cikin tsarin CS suna bambanta sosai.Wannan ya faru ne saboda bambance-bambancen yanayi na waɗannan tsarin da kuma sanya nau'o'i daban-daban kamar bawuloli, tarkuna da sauran kayan haɗi waɗanda zasu iya haifar da yanayi mai lalacewa da samfurori na lalata.
Bugu da ƙari, ana shigar da abubuwan maye gurbin sau da yawa a cikin tsarin waɗanda ba su da kyau sosai.Kayayyakin lalata kuma suna da tasiri sosai saboda ƙirar janareta na CS da ingancin ruwa.Wasu nau'ikan saitin janareta masu sake tafasawa ne yayin da wasu masu walƙiya tubular.CS janareta yawanci amfani da ƙarshen fuska don cire danshi daga tsabtataccen tururi, yayin da sauran janareta na amfani da baffles ko cyclones.
Wasu suna samar da patina mai ƙarfi na ƙarfe kusan a cikin bututun rarraba da jan ƙarfen da ke rufe shi.Tushen da aka ruɗe ya samar da fim ɗin baƙin ƙarfe na baƙin ƙarfe tare da baƙin ƙarfe oxide blush a ƙarƙashinsa kuma yana haifar da sabon abu na saman saman na biyu a cikin nau'in blush na sooty mai sauƙin gogewa daga saman.
A matsayinka na mai mulki, wannan ajiya mai kama da ferruginous-soot ya fi bayyana fiye da jan ƙarfe, kuma ya fi wayar hannu.Saboda karuwar yanayin oxidation na ƙarfe a cikin condensate, sludge da aka samar a cikin tashar condensate a kasan bututun rarraba yana da sludge na baƙin ƙarfe a saman sludge na ƙarfe.
Rashin baƙin ƙarfe oxide blush ya ratsa ta cikin mai tarawa, ya zama bayyane a cikin magudanar ruwa, kuma ana iya goge saman saman daga saman.Ingancin ruwa yana taka muhimmiyar rawa a cikin sinadarai na blush.
Babban abun ciki na hydrocarbon yana haifar da zuƙowa da yawa a cikin lipstick, yayin da mafi girman abun ciki na silica yana haifar da mafi girman abun ciki na silica, yana haifar da layin lipstick mai santsi ko mai sheki.Kamar yadda aka ambata a baya, gilashin kallon matakin ruwa shima yana da saurin lalacewa, yana barin tarkace da silica su shiga cikin tsarin.
Bindigar ta zama abin damuwa a tsarin tururi kamar yadda yadudduka masu kauri ke iya haifar da su.Wadannan barbashi suna nan a saman tururi ko a cikin kayan aikin haifuwa.Sassan da ke gaba sun bayyana yiwuwar tasirin magunguna.
As-Is SEMs a cikin Figures 7 da 8 suna nuna yanayin microcrystalline na nau'in carmine na aji 2 a yanayin 1. Musamman matrix mai yawa na lu'ulu'u na baƙin ƙarfe oxide da aka kafa a saman a cikin nau'i na raguwa mai kyau.Filayen da aka gurɓata da waɗanda ba su wuce gona da iri sun nuna lalacewar lalacewa wanda ya haifar da wani yanayi mai ɗanɗano da ɗan raɗaɗi kamar yadda aka nuna a Figures 9 da 10.
NPP scan a cikin fig.11 yana nuna yanayin farko na farfajiyar asali tare da baƙin ƙarfe mai nauyi akan sa. Wurin da aka wuce da shi (Hoto 12) yana nuna cewa fim ɗin mai wucewa yanzu yana da abun ciki mai ɗaukaka Cr (layin ja) sama da Fe (layin baƙar fata) a> 1.0 Cr: Fe. Wurin da aka wuce da shi (Hoto 12) yana nuna cewa fim ɗin mai wucewa yanzu yana da abun ciki mai ɗaukaka Cr (layin ja) sama da Fe (layin baƙar fata) a> 1.0 Cr: Fe. Пассивированная обесточенная поверхность (рис. 12) красная линия) по сравнению с Fe (черная линия) при соотношении Cr: Fe > 1,0. Wurin da aka yi amfani da shi da kuma ba da wutar lantarki (Fig. 12) yana nuna cewa fim din da aka yi amfani da shi a yanzu yana da karuwar abun ciki na Cr (layin ja) idan aka kwatanta da Fe (layin baki) a wani rabo na Cr: Fe> 1.0.钝化和去皱表面（图12）表明，钝化膜现在的Cr（红线）含量高于Fe（黑线）） 1:1 Cr（红线）含量高于Fe（黑线），Cr:Fe 比率> 1.0. Пассивированная е Cr (красная линия), чем Fe (черная линия), при соотношении Cr: Fe > 1,0. Wurin da aka wuce da kuma wrinkled (Fig. 12) yana nuna cewa fim ɗin da aka wuce yanzu yana da babban abun ciki na Cr (layin ja) fiye da Fe (layin baki) a Cr: Fe ratio> 1.0.
Fim ɗin chromium oxide mai wucewa (< 80 Å) mai wucewa ya fi karewa fiye da ɗaruruwan angstrom lokacin farin ciki crystalline baƙin ƙarfe oxide fim daga tushe karfe da sikelin Layer tare da abun ciki na baƙin ƙarfe fiye da 65%.
Abubuwan da ke tattare da sinadarai na farfajiyar da ke wucewa da kuma wrinkled yanzu sun yi kama da kayan goge goge.Lalacewar idan ta 1 ta kasance laburare ne na aji 2 wanda zai iya samuwa a wurin;yayin da yake taruwa, manyan ɓangarorin suna yin ƙaura da tururi.
A wannan yanayin, lalatar da aka nuna ba zai haifar da lahani mai tsanani ko lalacewar ingancin saman ba.Wrinkling na al'ada zai rage tasirin lalacewa a saman kuma ya kawar da yiwuwar ƙaura mai ƙarfi na barbashi waɗanda zasu iya zama bayyane.
A cikin hoto na 11, sakamakon AES ya nuna cewa ƙananan yadudduka kusa da saman suna da matakan Fe da O (500 Å na baƙin ƙarfe oxide; lemun tsami kore da blue Lines, bi da bi), canzawa zuwa matakan doped na Fe, Ni, Cr, da O. Fe maida hankali (layin blue) ya fi girma fiye da na kowane karfe, yana karuwa daga 35% a saman zuwa fiye da 65% a cikin allo.
A saman, matakin O (layin kore mai haske) yana tafiya daga kusan 50% a cikin gami zuwa kusan sifili a kauri na fim oxide fiye da 700 Å. Matakan Ni (layin kore mai duhu) da Cr (layin ja) suna da ƙasa sosai a saman (<4%) kuma suna ƙaruwa zuwa matakan al'ada (11% da 17%, bi da bi) a zurfin gami. Matakan Ni (layin kore mai duhu) da Cr (layin ja) suna da ƙasa sosai a saman (<4%) kuma suna ƙaruwa zuwa matakan al'ada (11% da 17%, bi da bi) a zurfin gami. Уровни Ni ( темно-зеленая линия) и Cr 17% соответственно) в глубине сплава. Matakan Ni (layin duhu mai duhu) da Cr (layin ja) suna da ƙasa sosai a saman (<4%) kuma suna ƙaruwa zuwa matakan al'ada (11% da 17% bi da bi) zurfi a cikin gami.表面的Ni（深绿线）和Cr（红线）水平极低（< 4%），而在合金深度处增加到到到平1% 17%)表面的Ni（深绿线）和Cr（红线）水平极低（< 4%），而在合金深度处增加到处增加到到歌平1% Уровни Ni ( темно-зеленая линия) и Cr бине сплава (11% da 17% соответственно). Matakan Ni (layin duhu mai duhu) da Cr (layin ja) a saman suna da ƙasa sosai (<4%) kuma suna ƙaruwa zuwa matakan al'ada a cikin gami (11% da 17% bi da bi).
Hoton AES a cikin fig.12 yana nuna cewa an cire ruwan rouge (iron oxide) kuma an dawo da fim ɗin wucewa.A cikin Layer na farko na 15 Å, matakin Cr (layin ja) ya fi matakin Fe (layin baki), wanda shine fim mai wucewa.Da farko, abun ciki na Ni a saman ya kasance 9%, yana ƙaruwa da 60-70 Å sama da matakin Cr (± 16%), sa'an nan kuma ƙara zuwa matakin allo na 200 Å.
Farawa daga 2%, matakin carbon (layin shuɗi) ya faɗi zuwa sifili a 30 Å. Matsayin Fe shine farkon ƙananan (<15%) kuma daga baya daidai da matakin Cr a 15 Å kuma ya ci gaba da karuwa zuwa matakin allo a fiye da 65% a 150 Å. Matsayin Fe shine farkon ƙananan (<15%) kuma daga baya daidai da matakin Cr a 15 Å kuma ya ci gaba da karuwa zuwa matakin allo a fiye da 65% a 150 Å. Уровень Fe вначале низкий (< 15%), позже равен уровню Cr при 15 Å Å. Matsayin Fe yana da ƙasa da farko (<15%), daga baya yayi daidai da matakin Cr a 15 Å kuma ya ci gaba da karuwa zuwa sama da 65% alloy matakin a 150 Å. Fe 含量最初很低(< 15%)，后来在15 Å 时等于Cr 含量，并在150 Å 时继续增加到超过过65% Fe 含量最初很低(< 15%)，后来在15 Å 时等于Cr 含量，并在150 Å 时继续增加到超过过65% Содержание Fe изначально низкое (< 15 %), позже оно равняется 65% zuwa 150 Å. Abun abun ciki na Fe yana da ƙasa da farko (<15%), daga baya yana daidai da abun ciki na Cr a 15 Å kuma yana ci gaba da haɓaka har sai abun ciki na gami ya wuce 65% a 150 Å.Matakan Cr suna ƙaruwa zuwa 25% na saman a 30 Å kuma suna raguwa zuwa 17% a cikin gami.
Madaidaicin matakin O kusa da saman (layin kore mai haske) yana raguwa zuwa sifili bayan zurfin 120 Å.Wannan bincike ya nuna ingantaccen fim ɗin wucewar ƙasa.Hotunan SEM a cikin adadi na 13 da 14 suna nuna ƙaƙƙarfan yanayi, ƙaƙƙarfan ƙaƙƙarfan yanayi na ɗigon ƙarfe na 1st da 2nd baƙin ƙarfe oxide.Fuskar da aka murɗe tana nuna tasirin lalata a kan wani yanki mara kyau (Hoto na 18-19).
Fuskokin da ba su da ƙarfi da murƙushe da aka nuna a cikin adadi na 13 da 14 ba sa jure yanayin iskar oxygen mai tsanani.Figures 15 da 16 suna nuna fim ɗin wucewa da aka dawo akan wani ƙarfe.