Faafetai mo le asiasi i le Nature.com.O le browser version o loʻo e faʻaogaina e faʻatapulaʻaina le lagolago mo le CSS.Mo le poto sili ona lelei, matou te fautuaina e te faʻaogaina se suʻesuʻega faʻafouina (pe tape le tulaga fetaui i Internet Explorer).
20MnTiB uʻamea o le mea sili ona faʻaaogaina faʻapipiʻi malosi maualuga mo alalaupapa fausaga uʻamea i loʻu atunuu, ma o lona faatinoga e taua tele i le faagaoioiga saogalemu o alalaupapa. E faavae i luga o le suesuega o le siosiomaga o le ea i Chongqing, o lenei suesuega fuafuaina se vaifofo corrosion simulating le tau susū o Chongqing, ma faia le mamafa o le susū susū o Chongqing, ma faia le mamafa o le susū susū suʻega o Chongqing, ma faia ai le mamafa o le susū o le vevela o le Chongqing suega pH tau ma fa'ata'ita'iga fofo fa'a'a'a'a fa'atatau i le fa'amamafa fa'aleaga amio a 20MnTiB malosi-maualuga fa'amau sa su'esu'eina.
20MnTiB uʻamea o le sili ona faʻaaogaina maualuga-malosi mea faʻapipiʻi mo alalaupapa fausaga uʻamea i loʻu atunuu, ma o lona faatinoga o se taua tele i le faagaoioiga saogalemu o alalaupapa.Li et al.1 faʻataʻitaʻiina meatotino o 20MnTiB uʻamea masani ona faʻaaogaina i le vasega 10.9 malosi malosi i le maualuga o le vevela o le 20 ~ 700 ℃, ma maua ai le faʻalavelave faʻamalosi, malosi malosi, malosi faʻamalosi, modulus a Young, ma le faʻalauteleina.ma fa'aopoopoga fa'aopoopo.Zhang et al.2, Hu et al.3, ma isi, e ala i suʻesuʻega vailaʻau, suʻesuʻega faʻainisinia, suʻega microstructure, suʻesuʻega macroscopic ma microscopic o le filo filo, ma faʻaalia ai o le mafuaʻaga autu mo le gau o le malosi malosi e fesoʻotaʻi ma faʻaletonu filo, ma le faʻalavelaveina o filo.
O faʻamau malosi mo alalaupapa uʻamea e masani ona faʻaaogaina mo se taimi umi i totonu o se siosiomaga susu. Factors e pei o le maualuga o le susu, maualuga le vevela, ma le palapala ma le absorption o mea leaga i totonu o le siosiomaga e mafai ona faigofie ona mafua ai le pala o fausaga uʻamea. ufi malosi ma e oo lava i le mafua ai ona malepe.E oo mai i le taimi nei, e tele suʻesuʻega i luga o le aʻafiaga o le siosiomaga i luga o le faʻalavelave faʻaleagaina o mea. eseese concentrations o sulfide ions.Aghion et al.6 iloilo le faatinoga corrosion o mate- lafo magnesium alloy MRI230D i le 3.5% NaCl fofo e ala i le faatofu suʻega, suʻega masima masima, potentiodynamic polarization auiliiliga ma SSRT.Zhang et al.7 suʻesuʻe le amio mamafa corrosion o le 9Cr ma martensitic uʻamea suʻesuʻega metotia o le 9Cr ma martensitic suʻesuʻega faʻataʻitaʻiga faʻataʻitaʻiga o le chloride faʻaaogaina le SSRT. o uamea martensitic i potu temperature.Chen et al.8 suʻesuʻeina le faʻalavelave faʻaleagaina amioga ma le taʻeina o le X70 uamea i le faʻataʻitaʻiina o le sami palapala palapala o loʻo i ai le SRB i le vevela eseese e SSRT.Liu et al.9 faʻaaogaina le SSRT e suʻesuʻe ai le aafiaga o le vevela ma le fua faʻafefeteina i luga o le suasami faʻamalosia le faʻafefeteina o le 00Mr21Ni2N. 5 ~ 65 ℃ e leai se aafiaga taua i luga o le amioga corrosion popole o stainless steel.Lu et al.10 iloilo le tuai gau gausceptibility o faataitaiga ma togi eseese malosi tensile e se uta mate tolopoina gau gau ma SSRT.It ua fautuaina o le tensile malosi o 20MnTiB uamea ma 35VB uamea maualuga-malosi uʻamea e tatau ona pulea i le 1040-1190MPa. rosive siosiomaga, aʻo le faʻaogaina moni o le siʻosiʻomaga o le malosi maualuga e sili atu ona faigata ma e tele mea e aʻafia ai, e pei o le pH tau o le bolt.Ananya et al.11 su'esu'e le a'afiaga o ta'aloga si'osi'omaga ma meafaitino i totonu o le ala fa'a'a'a'a'a ma fa'apopoleina fa'ama'i ta'ei o u'amea u'amea duplex.Sunada et al.12 faʻatautaia le vevela o le potu malulu faʻamalosi suʻega taʻe i luga o SUS304 uamea i vaifofo vai o loʻo i ai H2SO4 (0-5.5 kmol / m-3) ma NaCl (0-4.5 kmol / m-3) .O aʻafiaga o le H2SO4 ma le NaCl i luga o ituaiga pala o SUS304 uamea na suʻesuʻeina foi le suʻesuʻega o le vevela o le SUS304, suʻesuʻega o le vevela o le SUS304, suʻesuʻeina o le vevela o le CO2. omiga ma taimi pala i luga o le mamafa corrosion susceptibility o A516 ipu mamafa uamea. Faʻaaogaina NS4 fofo o se vaifofo simulating vai, Ibrahim et al.14 suʻesuʻeina le aʻafiaga o le siʻosiʻomaga e pei o le bicarbonate ion (HCO) concentration, pH ma le vevela i luga o le faʻalavelave faʻafefe o le API-X100 pipeline uamea ina ua uma ona paʻu ese le coating.Shan et al.15 suʻesuʻeina le tulafono fesuiaiga o le atuatuvale corrosion ta'e susceptibility o austenitic uamea stainless 00Cr18Ni10 ma le vevela i lalo o tulaga vevela eseese (30 ~ 250 ℃) i lalo o le tulaga o le ala vai uliuli i le simulated koale-i-hydrogen laau e SSRT.Han et al.16 faʻaalia le hydrogen embrittlement faʻataʻitaʻiga faʻataʻitaʻiga faʻataʻitaʻiga faʻataʻitaʻiga faʻataʻitaʻiga SSRT faʻataʻitaʻiga faʻataʻitaʻiga faʻataʻitaʻiga o le SSRT. hao17 suʻesuʻeina le aafiaga o le pH, SO42-, Cl-1 i luga o le faʻalavelave faʻafefe amioga a le GH4080A alloy e SSRT. O iʻuga e faʻaalia ai o le maualalo o le pH tau, o le leaga o le faʻalavelave faʻafefeteina o le GH4080A alloy. E manino le faʻafefe o le faʻamaʻi i le Cl-1, ma e le maaleale i le vevela o le siosiomaga i le SO42-i. MnTiB uamea maualuga malosi.
Ina ia mafai ona iloa mafuaʻaga o le le manuia o faʻamalo maualuga o loʻo faʻaaogaina i alalaupapa, na faia ai e le tusitala se faasologa o suʻesuʻega. Na filifilia faʻataʻitaʻiga faʻamalosi malosi, ma o mafuaʻaga o le toilalo o nei faʻataʻitaʻiga na talanoaina mai le vaʻaiga o vailaʻau, gau microscopic morphology, fausaga metallographic ma mea faʻainisinia suʻesuʻega i le suʻesuʻega o le siʻosiʻomaga lata mai19, 20. fa'atusa le tau susū o Chongqing ua fuafuaina. Fa'ata'ita'iga fa'amasani fa'amalosi, fa'ata'ita'iga fa'amea eletise eletise ma fa'ata'ita'iga vaivai o le malosi maualuga i Chongqing fa'atusa susū tau na fa'atinoina. au'ili'iliga, ma mea e pala i luga.
Chongqing o loʻo i le itu i sautesisifo o Saina, le pito i luga o le Vaitafe o Yangtze, ma o loʻo i ai se tau malulu subtropical monsoon climate.The averesi faaletausaga vevela o 16-18 ° C, o le fua faatatau faaletausaga o le susū masani o le tele o 70-80%, o le la o itula faaletausaga e 1000-1400 itula, ma le pasene la e na o le 25%.
E tusa ai ma lipoti e fesoʻotaʻi ma le susulu o le la ma le vevela i Chongqing mai le 2015 i le 2018, o le averesi o le vevela o aso uma i Chongqing e maualalo ifo i le 17 ° C ma maualuga i le 23 ° C.O le maualuga o le vevela i luga o le alalaupapa tino o Chaotianmen Bridge i Chongqing e mafai ona oʻo atu i le 50 ° C ° C21,22. O le mea lea, o le maualuga o le vevela mo le suʻega faʻamaʻi faʻamalosi na faʻatulagaina i le 25 ° C ma le 50 ° C.
O le tau o le pH o le vaifofo faʻataʻitaʻi faʻataʻitaʻiga e fuafua tonu lava le aofaʻi o le H +, ae e le o lona uiga o le maualalo o le pH, o le faigofie lea o le pala. su'esu'ega23 ma le tulaga o le pH o vai timu faaletausaga i Chongqing.2010 i le 2018.
O le maualuga o le maualuga o le faʻaogaina o le faʻamaʻi faʻataʻitaʻiga, o le tele o mea ion i totonu o le faʻataʻitaʻiga faʻafefete faʻataʻitaʻiga, ma le tele o le faatosinaga i mea faitino. 0 × fa'ata'ita'iga fa'amea fa'a'a'amea fa'ato'a fa'atatau (20 ×) ma le 200 × fa'ata'ita'iga fa'ato'a fa'a'a'amea vaifofo fa'atatau (200 ×).
O le siosiomaga ma le vevela o le 25 ℃, pH tau o le 5.5, ma le faʻatonuga o le vaifofo corrosion simulated e sili ona latalata i le tulaga faʻaoga moni o faʻamau malosi-maualuga mo alalaupapa. Ae ui i lea, ina ia faʻavaveina le faagasologa o suʻega aʻa, o tulaga faʻataʻitaʻi ma le vevela o le 25 °C, o le pH o le 5.200000000000000000 faʻauʻuga o le faʻatonuga o le faʻasologa o le kulupu faʻataʻitaʻiga o le faʻasologa o le kulupu faʻataʻitaʻi × o le faʻaogaina o le faʻasologa o le kulupu faʻataʻitaʻiga o le kulupu faʻataʻitaʻi × 5.200. o le vevela, faʻatonuga poʻo le pH tau o le faʻataʻitaʻiga faʻamaʻi fofo i luga o le faʻalavelave faʻalavelave faʻaleagaina o paʻu malosi-maualuga sa suʻesuʻeina taʻitasi, o isi mea na tumau e le suia, lea na faʻaaogaina e avea ma tulaga faʻataʻitaʻi o le vaega e pulea faʻamatalaga.
E tusa ai ma le 2010-2018 atmospheric environment quality briefing na tuuina mai e le Chongqing Municipal Bureau of Ecology and Environment, ma faasino i vaega o timuga na lipotia i le Zhang24 ma isi tusitusiga na lipotia mai i Chongqing, o se vaifofo faʻamaʻi faʻataʻitaʻiina e faʻavae i luga o le faʻateleina o le maualuga o le SO42- na mamanuina. i le laulau 1:
O le faʻataʻitaʻiina o le faʻamaʻi faʻamaʻi ua saunia e ala i le faʻaogaina o le faʻaogaina o le vailaʻau e faʻaaoga ai suʻesuʻega suʻesuʻe ma vai faʻafefe.
Ina ia faʻataʻitaʻiina le susū o le tau i Chongqing, ua faʻapitoa le faʻaleleia o le suʻega masima ma fuafuaina25. E pei ona faʻaalia i le Ata 1, o meafaigaluega faʻataʻitaʻiga e lua faiga: o se masini faʻafefe masima ma se moli. vaega e aofia ai elemene fuaina o le vevela, lea e lagona le vevela i le potu suʻesuʻe.O le vaega pulea e aofia ai se microcomputer, lea e fesootai le vaega spray ma le vaega induction e pulea ai le faagasologa atoa faataitai.O le faiga moli ua faapipiiina i totonu o se potu suʻesuʻe masima masima e simulate le susulu o le la.O le faiga moli e aofia ai lamepa infrared ma se taimi pulea.At o le taimi lava e suʻesuʻe ai le vevela.
O faʻataʻitaʻiga faʻamaʻi faʻamalosi i lalo o le uta faifaipea na faʻatautaia e tusa ai ma le NACETM0177-2005 (Suʻesuʻega a le Fale Suʻesuʻe ole Sulfide Stress Cracking and Stress Corrosion Cracking Resistance of Metals in a H2S Environment). Faʻamama faʻamaʻi faʻataʻitaʻiga na muamua faʻamamaina i le acetone ma le faʻamamaina o masini ultrasonic e aveese ai toega o le suauʻu, ma faʻamago i totonu o le ogaumu mama. masini suʻesuʻe e faʻataʻitaʻiina le tulaga pala i le siosiomaga susū tau o Chongqing. E tusa ai ma le tulaga NACETM0177-2005 ma le masima masima faʻataʻitaʻiga faʻataʻitaʻiga GB / T 10,125-2012, o le mamafa faifaipea taimi suega corrosion i lenei suʻesuʻega o loʻo fuafua tutusa e 168 h.Tensile faʻataʻitaʻiga faʻataʻitaʻiga corrosion1 TS 168 tulaga eseese i le corrotension Tensile 8 TS 168 tulaga i le corrotension TS 8 TS 168 tulaga lautele. masini su'esu'e, ma o latou mea fa'ainisinia ma gau gaui sa su'esu'eina.
O le ata 1 o lo'o fa'aalia ai le macro-ma micro-morphology o le a'a o luga o fa'ata'ita'iga fa'amamafa fa'amalosi malosi maualuga i lalo o tulaga fa'aleaga eseese.2 ma le 3.
Macroscopic morphology o faʻataʻitaʻiga faʻamaʻi aʻa o 20MnTiB malosi maualuga i lalo o siʻosiʻomaga faʻamea faʻatusa eseese: (a) leai se pala;(b) 1 taimi;(c) 20 ×;(d) 200 ×;(e) pH3.5;(f) pH 7.5;(g) 50°C.
Micromorphology o oloa pala o 20MnTiB maualuga-malosi u'amea i si'osi'omaga fa'amea fa'atusa fa'atusa (100×): (a) 1 taimi;(b) 20 ×;(c) 200 ×;(d) pH3.5;(e) pH7 .5;(f) 50°C.
E mafai ona iloa mai le Ata 2a o le pito i luga o le faʻataʻitaʻiga faʻataʻitaʻiga malosi maualuga e leʻi faʻafefeteina o loʻo faʻaalia ai le susulu o le uʻamea e aunoa ma le faʻaleagaina. e leai se aafiaga ole vaifofo a'a ile luga ole fa'ata'ita'iga.O meafaitino e itiiti sona aafiaga.Ae ui i lea, i lalo o le tulaga o le 20 × uluai simulated corrosion solution concentration (Fig. 2c), ua ufitia atoa le pito i luga o le faʻataʻitaʻiga faʻamalosi malosi maualuga e se aofaiga tele o mea pala pala tan ma sina vaega itiiti o le corrosion.product enaena-mumu, e leai se luster metallic manino na maua, ma sa i ai se vaega itiiti o le corrosion enaena-uliuli i lalo o le 0 substrate. sion solution concentration (Fig. 2d), o le pito i luga o le faʻataʻitaʻiga o loʻo ufiufi atoa i mea enaena enaena, ma o mea enaena-uliuli e aliali mai i nisi o vaega.
A'o fa'aitiitia le pH i le 3.5 (Fig. 2e), o mea fa'a'ele'ele lanu enaena na sili ona tele i luga o fa'ata'ita'iga, ma o nisi o mea fa'ameamea na fa'amama.
O le ata 2g o loʻo faʻaalia ai aʻo faʻatupulaʻia le vevela i le 50 °C, o mea o loʻo i totonu o mea enaena-mūmū mumu i luga o le faʻataʻitaʻiga e faʻaitiitia faʻafuaseʻi, aʻo mea enaena lanu enaena e ufiufi ai luga o le faʻataʻitaʻiga i se vaega tele.
E pei ona faaalia i le Ata 3, i lalo o siosiomaga corrosion eseese, o oloa pala i luga o le 20MnTiB maualuga-malosi faʻamalosi faʻamalosi faʻamaʻi faʻataʻitaʻiga e manino lava delaminated, ma le mafiafia o le faʻaʻamea faʻatuputeleina ma le faateleina o le concentration o le tali simulated corrosion.I lalo o le tulaga o le vaega muamua o le corrosion e mafai ona vaevaeina i luga o le vaifofo e lua. o le vaega pito i fafo o mea pala e fa'asoa tutusa, ae o le tele o ta'e e aliali mai;o le vaega i totonu o se fuifui matatalafu o oloa corrosion. I lalo o le tulaga o le 20 × uluai simulated corrosion solution concentration (Fig. 3b), e mafai ona vaevaeina le paʻu i luga o le faʻataʻitaʻiga i ni laulau se tolu: o le pito i fafo o loʻo faʻasalalau tele oloa faʻamaʻi fuifui, lea e matala ma porous, ma e leai se puipuiga lelei;O le vaega ogatotonu o se mea fa'amea pala tutusa, ae o lo'o i ai ta'eta'ei manino, ma e mafai ona ui atu ion corrosion i ta'eta'e ma tafi le substrate;o le vaega i totonu o se lapisi oloa corrosion mafiafia e aunoa ma ta'e manino, lea ei ai se aafiaga lelei puipuia i luga o le substrate.I lalo o le tulaga o le 200 × uluai simulated corrosion solution concentration (Fig. 3c), e mafai ona vaevaeina le vaega pala i luga o le faʻataʻitaʻiga i ni laulau se tolu: o le pito i fafo o se mea manifinifi ma toniga oloa oloa;o le vaega ogatotonu e masani lava o le petal-foliga ma flake-foliga corrosion O le pito i totonu o se mea mafiafia oloa pala e aunoa ma manino ta'e ma pu, lea ei ai se aafiaga puipuia lelei i luga o le substrate.
E mafai ona vaaia mai le Ata 3d e faapea i le siosiomaga corrosion simulated o le pH 3.5, o loo i ai se numera tele o flocculent po o ni nila-pei o mea pala i luga o le mata o le 20MnTiB malosi-maualuga uʻa specimen.It ua taumatemate o nei oloa corrosion e tele lava γ-FeOOH ma se vaega itiiti o le α-FeOOH γ-FeOOH ma se vaega itiiti o le α-FeOOH o loo i ai interrosion.
E mafai ona iloa mai le Ata 3f e faapea ina ua faateleina le vevela i le 50 °C, e leai se mea manino mafiafia ele i totonu na maua i totonu o le fausaga o le corrosion layer, e taʻu mai ai o loʻo i ai avanoa i le va o le pala i le 50 °C, lea na mafua ai ona le atoatoa le ufiufiina o le substrate i oloa pala.E maua ai le puipuiga mai le fa'ateleina o mea e pala.
O mea faʻainisinia o paʻu malolosi i lalo o le mamafa o le mamafa o le avega i siʻosiʻomaga eseese o loʻo faʻaalia i le Laulau 2:
E mafai ona vaʻaia mai le laulau 2 o le masini masini o le 20mntib maualuga-malosi-malosi-malosi-malosi o le faʻafitauli o le faʻafitauli o le susu o le sipelaina o le tali, o le faʻailo o le faʻataʻitaʻiga na faʻaititia tele fua e latalata tele i le tulaga masani.
O le gau o morphologies o le 20MnTiB maualuga malosi faʻamalosi faʻamalosi faʻamaʻi faʻataʻitaʻiga i lalo o siosiomaga faʻaleagaina eseese o loʻo faʻaalia i le Ata 4, o le macro-morphology o le gau, o le fiber sone i le ogatotonu o le gau, le micro-morphological laugutu o le faʻataʻitaʻiga, ma le pito i luga o le faʻataʻitaʻiga.
Macroscopic ma microscopic fracture morphologies o 20MnTiB faʻataʻitaʻiga faʻamalosi malosi i totonu o siʻosiʻomaga faʻaleagaina faʻatusa (500×): (a) leai se pala;(b) 1 taimi;(c) 20 ×;(d) 200 ×;(e) pH3.5;(f) pH7.5;(g) 50°C.
E mafai ona iloa mai le Ata 4 o le gau o le 20MnTiB maualuga malosi faʻamalosi faʻamalosi faʻamaʻi faʻataʻitaʻiga i lalo o siʻosiʻomaga faʻaleagaina faʻataʻitaʻiga o loʻo maua ai se gau masani o ipu-cone.A fa'atusatusa i le fa'ata'ita'iga e le'i pala (Fig. 4a), e la'ititi lava le vaega tutotonu o le ta'ega alava., O le laugutu shear eria e sili atu. O lenei ua faaalia ai o le mea tau masini o mea ua matua faaleagaina pe a uma corrosion.With le faateleina o le conrosion solution concentration simulated, o lua i totonu o le alava eria i le ogatotonu o le gau faateleina, ma manino suaisu loimata na aliali mai. Ina ua faateleina le concentration i le 20 taimi o le uluai simulated corrosion solution, e foliga mai o le corrosion vaifofo i le va o le faʻataʻitaʻiga faʻataʻitaʻiga i le va o le faʻataʻitaʻiga o le faʻataʻitaʻiga o le faʻataʻitaʻiga i le va o le faʻataʻitaʻiga o le faʻataʻitaʻiga ma le faʻataʻitaʻiga i le va o le faʻataʻitaʻiga o le faʻataʻitaʻiga i le va o le faʻataʻitaʻiga o le faʻataʻitaʻiga. le tele o mea e pala i luga.fa'ata'ita'i.
O loʻo faʻaalia mai le Ata 3d o loʻo i ai ni taʻetaʻe manino i totonu o le faʻaʻaʻamea i luga o le faʻataʻitaʻiga, e le o iai se puipuiga lelei i luga o le matrix.I le vaifofo faʻamaʻi faʻataʻitaʻiina o le pH 3.5 (Ata 4e), o le pito i luga o le faʻataʻitaʻiga ua matua pala, ma o le ogatotonu o le alava e manino lava laʻititi., O loʻo i ai se numera tele o suʻega loimata le masani i le ogatotonu o le eria fiber. Faatasi ai ma le faʻaopoopoga o le tau o le pH o le faʻataʻitaʻiina o le vaifofo faʻafefete, o le sone loimata i totonu o le fiber eria i le ogatotonu o le gau e faʻaitiitia, faʻaitiitia le lua, ma faʻaitiitia ai foi le loloto o le lua.
Ina ua siitia le vevela i le 50 °C (Fig. 4g), o le laugutu sele vaega o le gau o le faʻataʻitaʻiga na sili ona telē, o lua i totonu o le ogatotonu o le alava na faʻatupulaia tele, ma faʻateleina foi le loloto o le lua, ma faʻateleina le fesoʻotaʻiga i le va o le pito laugutu ma le faʻataʻitaʻiga.Ua fa'atupula'ia mea a'a ma lua, lea na fa'amaonia ai le fa'alolotoina o le a'a o mea e pei ona atagia i le Ata 3f.
O le taua o le pH o le vaifofo corrosion o le a mafua ai le faaleagaina o mea faʻainisinia o 20MnTiB malosi malosi, ae o le aʻafiaga e le taua. i le microscopic morphology o le gau faʻataʻitaʻiga. O lenei mea o loʻo faʻaalia ai o le malosi o le faʻataʻitaʻiga e tetee atu ai i le faʻaleagaina e le malosi mai fafo e faʻaititia tele i totonu o se siosiomaga acidic, ma o le tikeri o le faʻalavelave faʻalavelave faʻaleagaina o mea e matua faateleina.
O le vaifofo faʻamaʻi faʻataʻitaʻiina muamua e itiiti sona aʻafiaga i mea faʻainisinia o faʻataʻitaʻiga faʻamalosi malosi, ae a o faʻateleina le faʻaogaina o le vaifofo faʻataʻitaʻiina i le 20 taimi nai lo le vaifofo faʻameamea faʻataʻitaʻi muamua, o mea faʻainisinia o faʻataʻitaʻiga na matua faʻaleagaina, ma e manino lava le pala i le microstructure gau.lua, ta'eta'e lua ma le tele o mea pala. Ina ua fa'atuputeleina le fa'a'au'au fa'amea fa'atusa fa'atusa mai le 20 taimi i le 200 taimi o le fa'ata'ita'iga fa'ameamea fa'ameamea, na fa'avaivaia ai le a'afiaga o le fa'aogaina o mea fa'ainisinia.
A o le vevela corrosion simulated o le 25 ℃, o le malosi e maua mai ma le malosi tensile o le 20MnTiB maualuga-malosi faʻataʻitaʻiga faʻamau e le suia tele pe a faatusatusa i le uncorroded specimens.Ae ui i lea, i lalo o le simulated corrosion vevela vevela o le 50 °C, o le tensile malosi ma elongation o le vaega faʻataʻitaʻiga sa faʻaititia tele latalata i le faʻataʻitaʻiga sa faʻaitiitia le faʻaitiitia o le faʻataʻitaʻiga o le vaega faʻataʻitaʻiga na faʻaititia tele i lalo. le tele, ma sa i ai dimples i totonu o le eria alava tutotonu. Faateleina faateleina, loloto lua faateleina, oloa corrosion ma corrosion lua faateleina. O lenei e faaalia ai o le vevela synergistic corrosion siosiomaga ua i ai se aafiaga tele i le mea tau masini o ufi malosi-maualuga, lea e le o manino i le vevela o le potu, ae sili atu ona taua pe a oʻo le vevela 50 °C.
A maeʻa le suʻega faʻafefete faʻavave i totonu e faʻataʻitaʻiina le siosiomaga o le ea i Chongqing, o le malosi o le tensile, malosi e maua ai, faʻalauteleina ma isi faʻamaufaʻailoga o le 20MnTiB malosi malosi faʻaitiitia na faʻaitiitia, ma faʻaleagaina faʻalavelave faʻafuaseʻi. i paʻu malosi-maualuga, faʻaitiitia le malosi e tetee atu ai i le faʻaleagaina e le malosi mai fafo, ma faʻateleina le faʻalavelave o le faʻalavelave faʻafefe.
Li, G., Li, M., Yin, Y. & Jiang, S. Su'esu'ega fa'ata'ita'iga i mea totino o fa'amau malolosi e faia i le u'amea 20MnTiB i le vevela maualuga.jaw.Civil engineering.J.34, 100–105 (2001).
Hu, J., Zou, D. & Yang, Q. Su'esu'ega gau gau o 20MnTiB uamea maualuga-malosi u'amea mo rail.vevela togafitiga.Metal.42, 185-188 (2017).
Catar, R. & Altun, H. Stress corrosion ta'e amioga o alloys Mg-Al-Zn i lalo tulaga pH eseese e ala SSRT method.Open.Chemical.17, 972-979 (2019).
Nazer, AA et al.Aafiaga o le glycine i le electrochemical ma stress corrosion ta'e amioga o le u'amea Cu10Ni i sulfide-contaminated brine.Industrial Engineering.Chemical.reservoir.50, 8796-8802 (2011).
Aghion, E. & Lulu, N. Mea fa'a'a'a'a ole pa'u magnesi mate-fa'amea MRI230D i Mg(OH)2-tumu 3.5% NaCl solution.alma mater.character.61, 1221-1226 (2010).
Zhang, Z., Hu, Z. & Preet, MS Aafiaga o ion chloride i luga o amioga fa'a'ale'a ma fa'amamafa o le 9Cr martensitic steel.surf.Technology.48, 298–304 (2019).
Chen, X., Ma, J., Li, X., Wu, M. & Pese, B. Synergistic aafiaga o le SRB ma le vevela i luga o le atuatuvale corrosion ta'e o X70 uamea i fofo palapala palapala.J.Chin.Socialist Party.coros.Pro.39, 477–484 (2019).
Liu, J., Zhang, Y. & Yang, S. Fa'amamafa amioga a'a o 00Cr21Ni14Mn5Mo2N uamea u'amea i seawater.physics.su'e su'ega.test.36, 1-5 (2018).
Lu, C. O se su'esu'ega gau gau o le alalaupapa maualuga-malosi bolts.jaw.Academic school.rail.science.2, 10369 (2019).
Ananya, B. Fa'amamafa le ta'e o u'amea u'amea lua i vaifofo fa'ama'i. Fa'amatalaga Fa'a Fomai, Atlanta, GA, ISA: Georgia Institute of Technology 137-8 (2008)
Sunada, S., Masanori, K., Kazuhiko, M. & Sugimoto, K. Aafiaga o H2SO4 ma naci concentrations i luga o le mamafa corrosion ta'e o SUS304 uamea stainless i H2SO4-NaCl vai solution.alma mater.trans.47, 364-370 (2006).
Merwe, JWVD A'afiaga o le si'osi'omaga ma meafaitino i luga o le fa'apopoleina o le fa'afefe o le sila i le H2O/CO/CO2 solution.Inter Milan.J.Koros.2012, 1-13 (2012).
Ibrahim, M. & Akram A. Aafiaga o le bicarbonate, vevela ma le pH i luga o le passivation o API-X100 pipeline uamea i le simulated vai vaifofo.In IPC 2014-33180.
Shan, G., Chi, L., Pese, X., Huang, X. & Qu, D. Aafiaga o le vevela i le atuatuvale corrosion ta'e susceptibility o austenitic stainless steel.coro.be tetee i.Technology.18, 42–44 (2018).
Han, S. Hydrogen-fa'atupu fa'atuai gau gau o nisi maualuga-malosi u'amea u'amea (Kunming Iunivesite o Saienisi ma Tekonolosi, 2014).
Zhao, B., Zhang, Q. & Zhang, M. Stress corrosion mechanism of GH4080A alloy mo fasteners.cross.companion.Hey.treat.41, 102–110 (2020).
Taimi meli: Feb-17-2022