Nidaamyada dawooyinka uumiga saafiga ah ama saafiga ah waxaa ka mid ah koronto-dhaliyeyaasha, valves-ka kantaroolka, tuubooyinka qaybinta ama dhuumaha, dabinada heerkulbeegga ama dheellitirka heerkulbeegga, cabbirrada cadaadiska, cadaadiska yareeya, valves-ka badbaadada, iyo ururiyeyaasha mugga.
Inta badan qaybahan waxay ka samaysan yihiin 316 L bir ah oo aan lahayn waxayna ka kooban yihiin gaasaska fluoropolymer (sida caadiga ah polytetrafluoroethylene, oo sidoo kale loo yaqaan Teflon ama PTFE), iyo sidoo kale birta-biraha ah ama walxo kale oo elastomeric ah.
Qaybahan waxay u nugul yihiin daxalka ama hoos u dhaca inta lagu jiro isticmaalka, kaas oo saameeya tayada tamarta nadiifka ah ee nadiifka ah (CS).Mashruucu oo lagu faahfaahiyay maqaalkan wuxuu qiimeeyay muunado bir-la'aan ah oo laga helay afar daraasadood oo kiis oo nidaam CS ah, oo la qiimeeyay halista saamaynta daxalka ee ka iman karta nidaamka iyo nidaamyada injineernimada muhiimka ah, oo lagu tijaabiyay qaybo iyo biraha kondensate.
Tusaalooyinka tuubooyinka daxalka leh iyo qaybaha nidaamka qaybinta ayaa la meeleeyaa si loo baaro alaabada daxalka.9 Kiis kasta oo gaar ah, xaaladaha dusha kala duwan ayaa la qiimeeyay.Tusaale ahaan, midabada caadiga ah iyo saamaynta daxalka ayaa la qiimeeyay.
Dusha sare ee shaybaarada tixraaca ayaa lagu qiimeeyay joogitaanka kaydka guduudan iyadoo la isticmaalayo kormeer muuqaal ah, Auger electron spectroscopy (AES), electron spectroscopy for chemical analysis (ESCA), scanning microscopy elektarooniga ah (SEM) iyo raajada photoelectron spectroscopy (XPS).
Hababkani waxay muujin karaan sifooyinka jirka iyo atomiga ah ee daxalka iyo kaydka, iyo sidoo kale go'aaminta qodobbada muhiimka ah ee saameeya sifooyinka dareeraha farsamada ama alaabta dhamaadka.mid
Badeecooyinka daxalka ah ee birta aan la taaban karin waxay yeelan karaan qaabab badan, sida lakabka carmine ee oxide birta (brown ama cas) oo ku yaal dusha hoose ama ka sarreeya lakabka birta oksaydhka (madow ama cawl)2.Awoodda u haajiridda hoosteeda.
Lakabka oxide-ka birta ah (blush madow) ayaa laga yaabaa inuu dhumucdo wakhti ka dib marka kaydku noqdaan kuwo aad u muuqda, sida caddaynta qaybo ama kaydka ka muuqda dusha sare ee qolka jeermiska iyo qalabka ama weelasha ka dib jeermiska uumiga, waxaa jira guuritaan.Falanqaynta shaybaarka ee shaybaarada kondensate waxay muujisay dabeecadda kala firirsan ee dhoobada iyo cadadka biraha milmay ee dareeraha CS.afar
Inkasta oo ay jiraan sababo badan oo dhacdadan ah, koronto-dhaliyaha CS-ga ayaa badanaa ah ka qaybqaataha ugu weyn.Maaha wax aan caadi ahayn in la helo oksaydhka birta cas (brown/cas) ee dusha sare iyo birta oxide (madow/cawlan) ee hawo-mareenada si tartiib tartiib ah ugu guura nidaamka qaybinta CS.6
Nidaamka qaybinta CS waa qaabayn laamo leh oo leh dhibco badan oo la isticmaalo oo ku dhamaanaya meelaha fog fog ama dhamaadka madax-hoosaadka laanta kala duwan.Nidaamku waxa uu ku jiri karaa tiro nidaamiyayaal ah si ay u caawiyaan bilawga cadaadiska/dhimista heerkulka meelaha gaarka ah ee isticmaalka kuwaas oo noqon kara dhibco daxalka.
Daxalka waxa kale oo uu ku dhici karaa dabinada naqshadaynta nadaafadda ee la dhigo meelo kala duwan oo nidaamka si looga saaro uumiga iyo hawada ka soo qulqulaya uumiga nadiifka ah ee dhex mara dabinka, tuubooyinka hoose/tubooyinka daadinta ama madaxa kondensate.
Inta badan, guuritaanka rogaal celiska ah waxay u badan tahay halka kaydka miridhku ay ku dhismaan dabinka oo ay kor ugu soo baxaan ama ka baxaan dhuumaha ku xiga ama meelaha la isticmaalo;miridhku ka samaysma dabinnada ama qaybaha kale waxa laga arki karaa korka isha iyada oo guuritaan joogto ah hoos iyo kor.
Qaybo ka mid ah birta aan la taaban karin ayaa sidoo kale soo bandhiga heerar kala duwan oo dhexdhexaad ah ilaa heerar sare ah oo dhismayaal bir ah, oo ay ku jiraan delta ferrite.Kiristaalo Ferrite ayaa la rumeysan yahay inay yareeyaan iska caabinta daxalka, inkastoo laga yaabo inay ku jiraan wax yar 1-5%.
Ferrite sidoo kale uma adkeysato daxalka sida qaab dhismeedka crystal austenitic, sidaas darteed waxay doorbidi doontaa inay daxaleysato.Ferrites si sax ah ayaa loogu ogaan karaa baaritaanka ferrite iyo semi-sax ah oo leh magnet, laakiin waxaa jira xaddidaadyo muhiim ah.
Laga soo bilaabo habaynta nidaamka, iyada oo loo marayo hawlgelinta bilowga ah, iyo bilaabista koronto-dhaliye cusub oo CS ah iyo tuubooyinka qaybinta, waxaa jira dhowr arrimood oo gacan ka geysta daxalka:
Waqti ka dib, walxaha daxalka sida kuwan oo kale waxay soo saari karaan alaabada daxalka marka ay kulmaan, isku daraan, iyo isku dhafka birta iyo birta.Danbas madow ayaa sida caadiga ah marka hore lagu arkaa koronto-dhaliyaha, ka dib waxa ay ka soo muuqataa tuubbooyinka dareeraha koronto-dhaliye iyo ugu dambeyntii inta lagu jiro nidaamka qaybinta CS.
Falanqaynta SEM ayaa la sameeyay si loo muujiyo qaab-dhismeedka yar-yar ee alaabada daxalka ee daboolaya dhammaan dusha sare ee leh crystals iyo qaybo kale.Dhabarka ama dusha hoose ee walxaha laga helay waxay ku kala duwan yihiin heerarka kala duwan ee birta (Jaantus. 1-3) ilaa muunado caadi ah, kuwaas oo ah silica/iron, ciid, vitreous, kayd isku mid ah (Jaantus. 4).Waxa kale oo la falanqeeyay dabinkii uumiga (Jaantus. 5-6).
Tijaabada AES waa hab lafo-gur ah oo loo isticmaalo in lagu go'aamiyo kimistariga dusha sare ee birta-la'aanta ah iyo in lagu ogaado caabbinta daxalka.Waxa kale oo ay muujinaysaa sii xumaanshaha filimka dadban iyo hoos u dhigista fiirsashada chromium ee filimka dadban sida dusha sare u sii xumaanayo sababtoo ah daxalka.
Si loo qeexo halabuurka aasaasiga ah ee dusha sare ee muunad kasta, AES scans (muuqaalka xoogga saarida walxaha dusha sare ee qoto dheer) ayaa la isticmaalay.
Goob kasta oo loo isticmaalo falanqaynta SEM iyo kordhinta ayaa si taxadar leh loo doortay si ay u bixiso macluumaadka gobollada caadiga ah.Daraasad kastaa waxay bixisay macluumaadka dhawrka lakab ee ugu sarreeya (oo lagu qiyaasay 10 angstroms [Å] lakabkiiba) ilaa qoto dheer ee daawaha birta (200-1000 Å).
Qaddar muhiim ah oo bir ah (Fe), chromium (Cr), nikkel (Ni), ogsijiin (O) iyo kaarboon (C) ayaa laga diiwaan geliyay dhammaan gobollada Rouge.Xogta AES iyo natiijooyinka ayaa lagu qeexay qaybta daraasadda.
Natiijooyinka guud ee AES ee xaaladaha bilowga ah waxay muujinayaan in oksaydheynta xooggan ay ku dhacdo shaybaarrada leh xaddi aan caadi ahayn oo sarreeya oo Fe iyo O (iron oxides) iyo maadada Cr ee hoose.Dhigaalkan casaanka leh ayaa keenaya in la sii daayo qaybo wasakhaysan kara badeecada iyo sagxadaha oogyada marka la taabto alaabta.
Ka dib markii blush-ka la saaray, shaybaarada "passivated" ayaa muujiyay soo kabashada dhamaystiran ee filimka dadban, iyadoo Cr uu gaadhay heerar ka sarreeya Fe, oo leh Cr: Fe saamiga dusha u dhexeeya 1.0 ilaa 2.0 iyo maqnaanshaha guud ee oksaydhka birta.
Meelo kala duwan oo qallafsan ayaa lagu falanqeeyay iyadoo la adeegsanayo XPS/ESCA si loo barbardhigo heerarka aasaasiga ah iyo xaaladaha oksaydhka ee Fe, Cr, sulfur (S), calcium (Ca), sodium (Na), fosfooraska (P), nitrogen (N), iyo O. iyo C (miiska A).
Waxaa jira farqi cad oo u dhexeeya Cr ka qiyamka u dhow lakabka passivation ilaa qiyamka hoose sida caadiga ah laga helo alloys-ka.Heerarka birta iyo chromium ee laga helay dusha sare waxay matalaan dhumucyo kala duwan iyo darajooyinka kaydadka rouge.Tijaabooyin XPS ah ayaa muujiyay koror Na, C ama Ca oogag qallafsan marka la barbar dhigo sagxadaha la nadiifiyay iyo kuwa aan la socon.
Tijaabada XPS waxay sidoo kale muujisay heerar sare oo C oo ah birta cas (madow) cas iyo sidoo kale Fe(x)O(y) (iron oxide) oo casaan ah.Xogta XPS faa'iido uma laha fahamka isbeddelada dusha sare inta lagu jiro daxalka sababtoo ah waxay qiimeysaa labadaba birta cas iyo birta salka.Tijaabooyin dheeri ah oo XPS ah oo leh muunado waaweyn ayaa loo baahan yahay si si sax ah loo qiimeeyo natiijooyinka.
Qorayaashii hore waxay sidoo kale ku adkaatay inay qiimeeyaan xogta XPS.10 Indho-indheynta goobta inta lagu jiro habka saarista ayaa muujisay in kaarboonku uu sarreeyo oo inta badan lagu saaro sifeynta inta lagu jiro habaynta.Mikrogarafyada SEM ee la qaaday ka hor iyo ka dib daawaynta ka saarista laalaabku waxay muujinayaan dhaawaca dusha sare ee kaydadkaas, oo ay ku jiraan godadka iyo porosity, kuwaas oo si toos ah u saameeya daxalka.
Natiijooyinka XPS ka dib bakhtiyeyaashu waxay muujiyeen in saamiga Cr: Fe ee dusha sare uu aad u sarreeyay markii filimka baabuurka dib loo sameeyay, taas oo yaraynaysa heerka daxalka iyo saamaynta xun ee kale ee dusha sare.
Muunadaha kuubanku waxay muujiyeen koror weyn oo ku yimid saamiga Cr: Fe ee u dhexeeya "sida uu yahay" oogada iyo sagxadda bannaan.Saamiyada hore ee Cr: Fe waxaa lagu tijaabiyay inta u dhaxaysa 0.6 ilaa 1.0, halka daawaynta daawaynta ka dib saamiyadu ay u dhexeeyeen 1.0 ilaa 2.5.Qiimaha birta dabaysha ee elektiroonigga ah iyo kuwa aan la dhaafin waxay u dhexeeyaan 1.5 iyo 2.5.
Shaybaarada lagu sameeyay hab-socod ka dib, qoto dheer ee ugu badnaan ee saamiga Cr: Fe (lagu aasaasay iyadoo la isticmaalayo AES) waxay u dhaxaysay 3 ilaa 16 Å.Waxay si fiican u barbar dhigaan xogta daraasadihii hore ee ay daabaceen Coleman2 iyo Roll.9 Dusha sare ee shaybaarada oo dhan waxay lahaayeen heerarka caadiga ah ee Fe, Ni, O, Cr, iyo C. Heerarka hoose ee P, Cl, S, N, Ca, iyo Na ayaa sidoo kale laga helay inta badan shaybaarada.
Hadhaagaani waa kuwa caadiga ah ee nadiifinta kiimikada, biyaha la sifeeyay, ama korantada.Falanqaynta dheeraadka ah, qaar ka mid ah wasakhaynta silikon ayaa laga helay dusha sare iyo heerar kala duwan oo ah crystal austenite laftiisa.Isha waxay u muuqataa inay tahay nuxurka silica ee biyaha/ uumiga, muraayadaha farsamaysan, ama muraayadaha aragga ee milmay ama xardhan ee unugyada jiilka CS.
Alaabooyinka daxalka ah ee laga helo nidaamyada CS ayaa lagu soo waramayaa inay aad u kala duwan yihiin.Tani waxay sabab u tahay xaaladaha kala duwan ee nidaamyadan iyo meelaynta qaybaha kala duwan sida valves, dabinada iyo qalabyada kale ee keeni kara xaaladaha daxalka iyo alaabta daxalka.
Intaa waxaa dheer, qaybaha beddelka ayaa inta badan lagu soo bandhigaa nidaamka kuwaas oo aan si habboon u socon.Alaabooyinka daxalka ayaa sidoo kale si weyn u saameeya naqshada koronto dhaliyaha CS iyo tayada biyaha.Qaar ka mid ah qalabka wax dhaliya ayaa ah dib-u-kiciyeyaal halka kuwa kalena ay yihiin fallaadhaha tuubada.Soosaarayaasha CS caadi ahaan waxay isticmaalaan shaashadaha dhamaadka si ay qoyaanka uga saaraan uumiga nadiifka ah, halka koronto-dhaliyeyaasha kale ay isticmaalaan baffles ama duufaano.
Qaarkood waxay soo saaraan bir adag oo ku dhow tuubada qaybinta iyo birta cas ee daboolaysa.Baloogga wareersan wuxuu sameeyaa filim bir madow ah oo leh bir oxide guduudan oo hoostiisa ah wuxuuna abuuraa ifafaale dusha sare ee labaad oo ah qaab guduudan sooty ah oo sahlan in la tirtiro dusha sare.
Sida caadiga ah, deebaajigan ferruginous-soot u eg ayaa aad uga dhawaaq badan kan birta-cas, waana ka guurguuran yahay.Sababtoo ah korodhka oksaydheynta birta ee kondensate-ka, dhoobada ka dhalata kanaalka kondensate ee hoose ee tuubada qaybinta waxay leedahay dhoobo oksijiin bir ah oo ku yaal dusha sare ee birta.
Birta oksaydhka birta ahi waxay dhex martaa ururiyaha kondensate-ka, waxa ay noqotaa mid ka dhex muuqata biya-mareenka, lakabka sarena si fudud ayaa looga xoqayaa dusha sare.Tayada biyuhu waxay door muhiim ah ka ciyaartaa isku dhafka kiimikaad ee buluuga.
Mawduuca kaarboon-karboonka ah ee sarreeya wuxuu keenaa dambas aad u badan oo lipstick ah, halka maadada silica ee sareysa ay keenayso maadada silica sare, taasoo keentay lakab siman ama dhalaalaya lipstick.Sida hore loo sheegay, muraayadaha aragga heerka biyaha ayaa sidoo kale u nugul daxalka, taas oo u oggolaanaysa qashinka iyo silica inay galaan nidaamka.
Qoriga ayaa sabab u ah welwelka hababka uumiga maadaama lakabyo qaro weyn ay sameysan karaan kuwaas oo sameysma qaybo.Qaybahani waxay ku yaalaan sagxadaha uumiga ama qalabka jeermiska ee uumiga.Qaybaha soo socdaa waxay qeexayaan saamaynta daroogada ee suurtogalka ah.
As-Is SEMs ee Jaantusyada 7 iyo 8 waxay muujinayaan dabeecadda microcrystalline ee fasalka 2 carmine haddii ay dhacdo 1. Matrix cufan gaar ahaan cufan ee kiriimyada birta ah ee ka sameysan dusha sare ee qaabka hadhaaga wanaagsan.Sagxadaha wasakhaysan iyo sagxadaha bannaanka ah ayaa muujiyay burburka daxalka kaas oo keenay qaab-dhismeed qallafsan oo xoogaa daloola sida ku cad jaantusyada 9 iyo 10.
Sawirka NPP ee fig.11 waxay muujinaysaa xaalada bilawga ah ee dusha asalka ah oo leh oksaydh bir ah oo culus. Dusha sare ee aan la daahin iyo kuwa la sii daayay (Jaantuska 12) ayaa tilmaamaya in filimka dadban uu hadda leeyahay nuxur sare oo Cr ah (khadka cas) oo ka sarreeya Fe (khadka madow) ee> 1.0 Cr: Fe. Dusha sare ee aan la daahin iyo kuwa la sii daayay (Jaantuska 12) ayaa tilmaamaya in filimka dadban uu hadda leeyahay nuxur sare oo Cr ah (khadka cas) oo ka sarreeya Fe (khadka madow) ee> 1.0 Cr: Fe. Пассивированная и обесточенная поверхность красная линия) по сравнению с Fe (черная линия) при соотношении Cr: Fe > 1,0. Dusha sare ee aan tamar lahayn iyo kuwa aan tamar lahayn (Jaantus. 12) waxay tilmaamaysaa in filimka dadban uu hadda leeyahay koodhka Cr (khadka cas) marka la barbar dhigo Fe (khadka madow) ee saamiga Cr: Fe> 1.0.钝化和去皱表面（图12）表明，钝化膜现在的Cr（红线）含量高于Fe（黑线）） 1:0. Cr（红线）含量高于Fe（黑线），Cr:Fe 比率> 1.0. Пассивированная скачать видео - е Cr (красная линия), чем Fe (черная линия), при соотношении Cr: Fe> 1,0. Dusha laalaabtay iyo laalaabtay (Jaantus. 12) waxay tusinaysaa in filimka baasbeelka ahi uu hadda leeyahay ka kooban Cr ka sarreeya (khadka cas) marka loo eego Fe (khadka madow) marka loo eego saamiga Cr: Fe> 1.0.
dhuuban (< 80 Å) filimka chromium oxide passivating waa ka difaac badan yahay boqollaal filim qaro weyn angstrom crystalline bir oxide filim ka bir salka iyo lakabka miisaanka leh content birta in ka badan 65%.
Halabuurka kiimikaad ee dusha laalaabtay iyo kan laalaabtay ayaa hadda la barbar dhigi kara walxaha la sifeeyay ee la sifeeyay.Dheecaanku haddii ay dhacdo 1 waa sediment fasalka 2 oo awood u leh in lagu sameeyo goobta;marka ay ururto, waxa samaysma qaybo waaweyn oo la haajiray uumiga.
Xaaladdan oo kale, daxalka la muujiyay ma horseedi doono cillado halis ah ama hoos u dhaca tayada dusha sare.Laalaabkii caadiga ahaa wuxuu yarayn doonaa saamaynta daxalka ah ee dusha sare waxayna meesha ka saaraysaa suurtagalnimada guuritaanka xooggan ee walxaha laga yaabo inay muuqdaan.
Jaantuska 11, natiijooyinka AES waxay muujinayaan in lakabyada qaro weyn ee dusha sare ay leeyihiin heerar sare oo Fe iyo O ah (500 Å of iron oxide; liin cagaarka iyo khadadka buluuga ah, siday u kala horreeyaan), u gudubka heerarka doped ee Fe, Ni, Cr, iyo O. Fe fiirsashada (khadka buluuga ah) ayaa aad uga sarreeya tan birta kale, oo ka kordhaysa 35% dusha sare ilaa 65% alloy
Dusha sare, heerka O (khadka cagaaran ee khafiifka ah) wuxuu ka yimaadaa ku dhawaad ​​50% alloy-ga ilaa eber ku dhawaad ​​dhumucdiisuna waxay tahay filim oksaydh ah oo ka badan 700 Å. Heerarka Ni (khadka cagaaran ee madow) iyo Cr (khadka cas) aad bay ugu hooseeyaan dusha sare (< 4%) waxayna kordheen ilaa heerar caadi ah (11% iyo 17%, siday u kala horreeyaan) ee gunta alloyka. Heerarka Ni (khadka cagaaran ee madow) iyo Cr (khadka cas) aad bay ugu hooseeyaan dusha sare (< 4%) waxayna kordheen ilaa heerar caadi ah (11% iyo 17%, siday u kala horreeyaan) ee gunta alloyka. Уровни Ni ( темно-зеленая линия) и Cr 17% соответственно) в глубине сплава. Heerarka Ni (khadka cagaaran ee mugdiga ah) iyo Cr (khadka cas) ayaa aad ugu hooseeya dusha sare (<4%) waxayna kordheen heerarka caadiga ah (11% iyo 17% siday u kala horreeyaan) qoto dheer ee daawaha.表面的Ni（深绿线）和Cr（红线）水平极低（< 4%），而在合金深度处增加到到到丆1%1 17%)表面的Ni（深绿线）和Cr（红线）水平极低（< 4%），而在合金深度处增加到处增加到到到平1% Уровни Ni ( темно-зеленая линия) и Cr бине сплава (11% iyo 17% соответственно). Heerarka Ni (khadka cagaaran ee madow) iyo Cr (khadka cas) ee dusha sare aad bay u hooseeyaan (<4%) waxayna kordheen ilaa heerarka caadiga ah ee qoto dheer ee daawaha (11% iyo 17% siday u kala horreeyaan).
Sawirka AES ee fig.12 waxay muujinaysaa in lakabka rouge (iron oxide) laga saaray oo filimkii passivation ayaa dib loo soo celiyay.Lakabka hoose ee 15 Å, heerka Cr (khadka cas) ayaa ka sarreeya heerka Fe (khadka madow), kaas oo ah filim dadban.Markii hore, nuxurka Ni ee dusha sare wuxuu ahaa 9%, wuxuu kordhay 60-70 Å oo ka sarreeya heerka Cr (± 16%), ka dibna wuxuu kordhay heerka alloy ee 200 Å.
Laga bilaabo 2%, heerka kaarboonka (khadka buluuga) wuxuu hoos ugu dhacayaa eber 30 Å. Heerka Fe markii hore wuu hooseeyaa (< 15%) ka dibna wuxuu la mid yahay heerka Cr ee 15 Å wuxuuna sii wadaa inuu kordho heerka alloy-ga oo ka badan 65% 150 Å. Heerka Fe markii hore wuu hooseeyaa (< 15%) ka dibna wuxuu la mid yahay heerka Cr ee 15 Å wuxuuna sii wadaa inuu kordho heerka alloy-ga oo ka badan 65% 150 Å. Уровень Fe вначале низкий (< 15%), позже равен уровню Cr при 15 Å Å. Heerka Fe markii hore wuu hooseeyaa (< 15%), ka dib wuxuu la mid yahay heerka Cr ee 15 Å wuxuuna sii wadaa inuu kordho 65% heerka alloy ee 150 Å. Fe 含量最初很低(< 15%)，后来在15 Å 时等于Cr 含量，并在150 Å. Fe 含量最初很低(< 15%)，后来在15 Å 时等于Cr 含量，并在150 Å. Содержание Fe изначально низкое (< 15 %), а более 65 % 150 Å. Maaddada Fe ayaa bilawga hooseeya (< 15%), ka dib waxay la mid tahay maadada Cr ee 15 Å wayna sii socotaa ilaa inta ay ka kooban tahay aluminiumku 65% 150 Å.Heerarka Cr ayaa kor u kaca ilaa 25% ee dusha sare ee 30 Å waxayna hoos ugu dhacaan 17% ee daawaha.
Heerka sare ee O ee u dhow dusha sare (khadka cagaaran ee iftiinka) wuxuu hoos ugu dhacayaa eber ka dib qoto dheer oo ah 120 Å.Falanqayntani waxay muujisay filim si fiican u horumarsan oo dusha sare ah.Sawirrada SEM ee jaantusyada 13 iyo 14 waxay muujinayaan qallafsanaanta, qallafsanaanta iyo dabeecadda crystalline ee dusha sare ee lakabyada 1aad iyo 2aad ee birta.Dusha laalaabtay waxay tusinaysaa saamaynta daxalka ee dusha qalafsan oo qayb ahaan go'an (Jaantus 18-19).
Dusha sare ee laalaabtay ee lagu muujiyey jaantusyada 13 iyo 14 uma adkeystaan ​​oksaydheynta daran.Jaantusyada 15 iyo 16 waxay muujinayaan filim dammaanad qaad ah oo la soo celiyay oo ku yaal dusha birta ah.