Sistimi e hloekileng kapa e hloekileng ea meriana ea mouoane e kenyelletsa lijenereithara, li-valve tsa taolo, liphaephe tsa kabo kapa liphaephe, maraba a thermodynamic kapa equilibrium thermostatic, likhakanyo tsa khatello, li-conduction tsa khatello, li-valve tsa polokeho le li-accumulators tsa volumetric.
Boholo ba likarolo tsena li entsoe ka tšepe e sa hloekang ea 316 L 'me li na le likhase tsa fluoropolymer (ka tloaelo polytetrafluoroethylene, e tsejoang hape e le Teflon kapa PTFE), hammoho le lisebelisoa tsa semi-metal kapa tse ling tsa elastomeric.
Likarolo tsena li kotsing ea ho bola kapa ho senyeha ha li sebelisoa, tse amang boleng ba sesebelisoa se felileng sa Clean Steam (CS).Morero o hlalositsoeng sehloohong sena o hlahlobile mehlala ea tšepe e sa hloekang ho tsoa liphuputsong tse 'nè tsa tsamaiso ea CS, ea hlahloba kotsi ea liphello tse ka bang teng tsa kutu tsamaisong ea ts'ebetso le mekhoa ea boenjiniere ea bohlokoa,' me ea lekoa bakeng sa li-particulate le tšepe ka condensate.
Mehlala ea likarolo tsa tsamaiso ea lipeipi tse jeoang le ho ajoa li behiloe ho batlisisa lihlahisoa tse tsoang ho tse ling.9 Bakeng sa nyeoe ka 'ngoe, maemo a fapaneng a holim'a metsi a ile a hlahlojoa.Mohlala, litlamorao tse tloaelehileng tsa blush le corrosion li ile tsa hlahlojoa.
Bokaholimo ba lisampole tsa litšupiso bo ile ba lekoa bakeng sa boteng ba li-depositi tse blush ho sebelisoa tlhahlobo ea pono, Auger electron spectroscopy (AES), electron spectroscopy bakeng sa tlhahlobo ea lik'hemik'hale (ESCA), scanning electron microscopy (SEM) le X-ray photoelectron spectroscopy (XPS).
Mekhoa ena e ka senola thepa ea 'mele le ea athomo ea kutu le li-deposit, hammoho le ho tseba lintlha tsa bohlokoa tse amang thepa ea maro a tekheniki kapa lihlahisoa tsa ho qetela.ngoe
Lihlahisoa tsa tšepe tse sa hloekang li ka nka mefuta e mengata, joalo ka carmine layer ea iron oxide (e sootho kapa e khubelu) ka holimo kapa ka holim'a lera la iron oxide (e ntšo kapa e bohlooho)2.Bokhoni ba ho fallela tlase.
The iron oxide layer (black blush) e ka 'na ea teteana ha nako e ntse e feta ha li-deposit li ntse li bonahala haholoanyane, joalokaha ho pakoa ke likaroloana kapa li-deposit tse bonahalang holim'a kamore ea sterilization le lisebelisoa kapa lijana ka mor'a hore ho be le sterilization ea mouoane, ho na le ho falla.Tlhahlobo ea laboratori ea lisampole tsa condensate e bontšitse sebopeho se qhalakaneng sa seretse le bongata ba litšepe tse qhibilihang ka har'a mokelikeli oa CS.nne
Le hoja ho na le mabaka a mangata a ketsahalo ena, jenereithara ea CS hangata ke eona e kenyang letsoho haholo.Ho tloaelehile ho fumana oxide ea tšepe e khubelu (e sootho / e khubelu) holim'a metsi le tšepe ea oxide (e ntšo / e putsoa) ka har'a li-vents tse tsamaeang butle-butle ka tsamaiso ea CS.6
Sistimi ea kabo ea CS ke tlhophiso ea makala e nang le lintlha tse ngata tsa tšebeliso e qetellang libakeng tse hole kapa qetellong ea sehlooho se seholo le lihloohoana tse fapaneng tsa makala.Tsamaiso e ka kenyelletsa balaoli ba 'maloa ho thusa ho qala khatello / phokotso ea mocheso lintlheng tse itseng tsa tšebeliso e ka' nang ea e-ba libaka tse ka senyang.
Corrosion e ka boela ea hlaha marabeng a bohloeki a moralo a behiloeng lintlheng tse fapaneng tsa sistimi ho tlosa condensate le moea ho tsoa mouoane o hloekileng ka leraba, piping / discharge piping kapa condensate header.
Maemong a mangata, ho falla ho ka 'na ha etsahala moo mafome a bokellanang holim'a leraba 'me a hola ho ea holimo le ka nqane ho liphaephe tse haufi kapa likoleke tsa tšebeliso;mafome a hlahang marabeng kapa dikarolong tse ding a ka bonoa hodimo ho mohlodi ka ho falla ho sa feleng ho theosa le ho nyolosa.
Likarolo tse ling tsa tšepe tse sa hloekang li boetse li bonts'a maemo a fapaneng a itekanetseng ho isa ho a phahameng a meaho ea metallurgical, ho kenyeletsoa delta ferrite.Likristale tsa Ferrite ho lumeloa hore li fokotsa ho hanyetsa ha kutu, leha li ka ba teng ka nako e nyane joalo ka 1-5%.
Ferrite le eona ha e hanyetsane le kutu joalo ka sebopeho sa kristale ea austenitic, ka hona e tla senya ka mokhoa o ikhethileng.Li-ferrite li ka bonoa ka nepo ka probe ea ferrite le ho nepahala ha halofo ka makenete, empa ho na le mefokolo e kholo.
Ho tloha ho tlhophiso ea sistimi, ka ts'ebetso ea pele, le ho qala ha jenereithara e ncha ea CS le liphaephe tsa kabo, ho na le lintlha tse 'maloa tse tlatsetsang ho bola:
Ha nako e ntse e ea, lintho tse senyang tse kang tsena li ka hlahisa lihlahisoa tse senyang ha li kopana, li kopana le ho kopana le metsoako ea tšepe le tšepe.Hangata mosili o motšo o bonoa pele ho jenereithara, ebe o hlaha ka har'a liphaephe tsa ho ntša jenereithara 'me qetellong ho pholletsa le tsamaiso ea CS.
Tlhahlobo ea SEM e ile ea etsoa ho senola microstructure ea li-corrosion by-products tse koahelang bokaholimo bohle ka likristale le likaroloana tse ling.Semelo kapa sebaka se ka tlase seo likaroloana li fumanoang ho sona se fapana ho tloha ho lihlopha tse sa tšoaneng tsa tšepe (setšoantšo sa 1-3) ho ea ho mehlala e tloaelehileng, e leng silica / iron, sandy, vitreous, homogeneous deposits (setšoantšo sa 4).Li-bellows tsa sefi sa mouoane le tsona li ile tsa hlahlojoa (setšoantšo sa 5-6).
Teko ea AES ke mokhoa oa tlhahlobo o sebelisetsoang ho tseba hore na k'hemistri e holim'a tšepe e sa hloekang le ho fumana hore na e hana ho bola.E boetse e bonts'a ho senyeha ha filimi e sa sebetseng le ho fokotseha ha bongata ba chromium filiming e sa sebetseng ha bokaholimo bo ntse bo senyeha ka lebaka la ho bola.
Ho bonts'a sebopeho sa mantlha sa sampole e 'ngoe le e' ngoe, ho ile ha sebelisoa litlhahlobo tsa AES (lintlha tsa mahloriso a likarolo tse holim'a botebo) li ile tsa sebelisoa.
Sebaka se seng le se seng se sebelisetsoang tlhahlobo ea SEM le ho eketsa se khethiloe ka hloko ho fana ka tlhahisoleseding e tsoang libakeng tse tloaelehileng.Phuputso e 'ngoe le e' ngoe e fane ka boitsebiso ho tloha likarolong tse seng kae tse ka holimo tsa limolek'hule (e hakanyetsoang ho 10 angstroms [Å] ka lera) ho ea botebong ba motsoako oa tšepe (200–1000 Å).
Likarolo tse kholo tsa tšepe (Fe), chromium (Cr), nickel (Ni), oxygen (O) le carbon (C) li tlalehiloe libakeng tsohle tsa Rouge.Lintlha tsa AES le liphetho li hlalositsoe karolong ea thuto ea linyeoe.
Liphetho tsa kakaretso tsa AES bakeng sa maemo a pele li bonts'a hore oxidation e matla e hlaha ka lisampole tse nang le likhahla tse phahameng tse sa tloaelehang tsa Fe le O (iron oxides) le litaba tse tlase tsa Cr holim'a metsi.Deposit ena e khubelu e fella ka ho lokolloa ha likaroloana tse ka silafatsang sehlahisoa le bokaholimo bo amanang le sehlahisoa.
Ka mor'a hore blush e tlosoe, li-sampuli tsa "passivated" li bontšitse ho hlaphoheloa ka ho feletseng ha filimi e sa sebetseng, 'me Cr e fihla maemong a phahameng a mahloriso ho feta Fe, e nang le Cr: Fe surface ratio ho tloha 1.0 ho ea 2.0 le ho ba sieo ha tšepe ea tšepe ka kakaretso.
Ho ile ha hlahlobjoa libaka tse fapa-fapaneng tse mahlahahlaha ho sebelisoa XPS/ESCA ho bapisa likarolo tsa elemental le spectral oxidation states of Fe, Cr, sulfur (S), calcium (Ca), sodium (Na), phosphorus (P), nitrogen (N), le O. le C (tafole A).
Ho na le phapang e hlakileng ho litaba tsa Cr ho tloha ho boleng bo haufi le sekhahla sa passivation ho ea ho boleng bo tlase bo fumanehang ka har'a li-alloys tsa motheo.Litekanyo tsa tšepe le chromium tse fumanehang ka holim'a metsi li emela botenya bo fapaneng le limaraka tsa rouge deposits.Liteko tsa XPS li bonts'itse keketseho ea Na, C kapa Ca libakeng tse makukuno ha li bapisoa le libaka tse hloekisitsoeng le tse sa kengoang.
Teko ea XPS e boetse e bonts'a maemo a phahameng a C a tšepe e khubelu (e ntšo) e khubelu hammoho le Fe(x)O(y) (iron oxide) e khubelu.Lintlha tsa XPS ha li na thuso ho utloisisa liphetoho tsa bokaholimo nakong ea kutu hobane e lekola tšepe e khubelu le tšepe ea motheo.Ho hlokahala liteko tse ling tsa XPS tse nang le lisampole tse kholo ho lekola liphetho hantle.
Bangoli ba nakong e fetileng le bona ba bile le bothata ba ho lekola lintlha tsa XPS.10 Litlhokomeliso tsa masimo nakong ea ts'ebetso ea ho tlosa li bontšitse hore carbon content e phahame 'me hangata e tlosoa ka ho hloekisa nakong ea ts'ebetso.Li-micrographs tsa SEM tse nkiloeng pele le ka mor'a phekolo ea ho tlosoa ha wrinkles li bontša tšenyo e holim'a metsi e bakoang ke li-deposit tsena, ho akarelletsa le pitting le porosity, tse amang kutu ka ho toba.
Liphetho tsa XPS ka mor'a passivation li bontšitse hore tekanyo ea Cr: Fe e ka holim'a metsi e ne e phahame haholo ha filimi ea passivation e tsosolosoa, kahoo e fokotsa sekhahla sa kutu le liphello tse ling tse mpe holim'a metsi.
Mehlala ea setlankane e bontšitse keketseho e kholo ea karolelano ea Cr: Fe pakeng tsa "joalokaha e le" holim'a metsi le sebaka se patisitsoeng.Likarolo tsa pele tsa Cr: Fe li ile tsa lekoa ho tloha ho 0.6 ho isa ho 1.0, ha likarohano tsa "post-passivation" tsa ka mor'a phekolo li ne li tloha ho 1.0 ho ea ho 2.5.Litekanyetso tsa litšepe tse se nang tšepe tse entsoeng ka elektropolished le passivated li pakeng tsa 1.5 le 2.5.
Mehlala e tlas'a ts'ebetso ea morao-rao, botebo bo boholo ba tekanyo ea Cr: Fe (e thehiloeng ho sebelisoa AES) e tloha ho 3 ho ea ho 16 Å.Ba bapisa hantle le lintlha tse tsoang lithutong tse fetileng tse phatlalalitsoeng ke Coleman2 le Roll.9 Bokaholimo ba lisampole kaofela bo ne bo e-na le maemo a tloaelehileng a Fe, Ni, O, Cr, le C. Maemo a tlaase a P, Cl, S, N, Ca, le Na le ’ona a ile a fumanoa boholong ba lisampole.
Masala ana a tloaelehile ho lihloekisi tsa lik'hemik'hale, metsi a hloekisitsoeng, kapa electropolishing.Ha ho hlahlojoa ho ea pele, ho ile ha fumanoa tšilafalo e 'ngoe ea silicon holim'a metsi le ka mekhahlelo e fapaneng ea kristale ea austenite ka boeona.Mohloli o bonahala e le silika ea metsi / mouoane, lipolisi tse entsoeng ka mochine, kapa likhalase tsa mahlo tse qhibilihisitsoeng kapa tse kentsoeng ka har'a sele ea moloko oa CS.
Lihlahisoa tsa Corrosion tse fumanoang lits'ebetsong tsa CS li tlalehoa li fapana haholo.Sena se bakoa ke maemo a sa tšoaneng a mekhoa ena le ho behoa ha likarolo tse sa tšoaneng tse kang li-valve, maraba le lisebelisoa tse ling tse ka lebisang ho maemo a senya le lihlahisoa tsa ho senya.
Ho phaella moo, likarolo tse ncha li atisa ho kenngoa tsamaisong e sa feteng hantle.Lihlahisoa tsa Corrosion li boetse li angoa haholo ke moralo oa jenereithara ea CS le boleng ba metsi.Mefuta e meng ea lisebelisoa tsa jenereithara ke li-reboiler ha tse ling e le li-flash tsa tubula.Lijenereithara tsa CS hangata li sebelisa li-screen screen ho tlosa mongobo mouoane o hloekileng, ha lijenereithara tse ling li sebelisa li-baffles kapa maholiotsoana.
Tse ling li hlahisa patina e batlang e tiile ka har'a phaephe ea kabo le tšepe e khubelu e e koahelang.Sebaka se ferekaneng se etsa filimi e ntšo ea tšepe e nang le iron oxide blush ka tlas'a eona 'me e etsa hore ho be le ntho ea bobeli e holimo ka mokhoa oa sooty blush eo ho leng bonolo ho e hlakola holim'a metsi.
E le molao, depositi ena e boreleli-e kang soot e bonahala haholo ho feta e khubelu ea tšepe, 'me e tsamaea haholoanyane.Ka lebaka la boemo bo ntseng bo eketseha ba oxidation ea tšepe ka har'a condensate, seretse se hlahisoang ka kanaleng ea condensate e ka tlase ho phala ea phepelo e na le seretse sa tšepe ea oxide ka holim'a seretse sa tšepe.
Blush ea iron oxide e feta har'a mokelli oa condensate, e bonahala ka har'a drain, 'me karolo e ka holimo e phunyeletsoa habonolo holim'a metsi.Boleng ba metsi bo phetha karolo ea bohlokoa mofuteng oa lik'hemik'hale oa blush.
Likahare tsa hydrocarbon tse phahameng li hlahisa soot e ngata haholo molomong oa molomo, ha silika e phahameng e hlahisa silika e phahameng, e hlahisang lesela le boreleli kapa le benyang.Joalokaha ho boletsoe pejana, likhalase tsa pono ea boemo ba metsi le tsona li na le tšekamelo ea ho bola, tse lumellang maloanlahla le silika ho kena tsamaisong.
Sethunya ke sesosa sa ho tšoenyeha ka litsamaiso tsa mouoane kaha masela a teteaneng a ka etsa likaroloana.Likaroloana tsena li teng holim'a libaka tsa mouoane kapa lisebelisoa tse thibelang mouoane.Likarolo tse latelang li hlalosa liphello tse ka bang teng tsa lithethefatsi.
The As-Is SEMs ho Figure 7 le 8 e bonts'a tlhaho ea microcrystalline ea sehlopha sa 2 carmine tabeng ea 1. Matrix e teteaneng ka ho khetheha ea likristale tsa tšepe tsa oxide tse entsoeng ka holim'a metsi ka mokhoa oa masala a mahlahahlaha.Libaka tse silafetseng le tse senyehileng li bonts'itse ts'enyeho ea kutu e bakang sebopeho sa bokaholimo bo makukuno joalo ka ha ho bonts'itsoe ho Lipalo 9 le 10.
Setšoantšo sa NPP ka feiga.11 e bonts'a boemo ba pele ba sebaka sa pele se nang le oxide e boima ea tšepe ho eona. Sebaka sa passivated le se senyehileng (Setšoantšo sa 12) se bontša hore filimi e sa sebetseng hona joale e na le Cr e phahameng (mola o mofubelu) ka holimo ho Fe (mola o motšo) ho> 1.0 Cr: Fe ratio. Sebaka sa passivated le se senyehileng (Setšoantšo sa 12) se bontša hore filimi e sa sebetseng hona joale e na le Cr e phahameng (mola o mofubelu) ka holimo ho Fe (mola o motšo) ho> 1.0 Cr: Fe ratio. Пассивированная и обесточенная поверхность (рис. 12) указывает на то, что пассивная пленка теперь имеет повышенное содержанися Круский я) при соотношении Cr:Fe > 1,0. Sebaka sa passivated and de-energized surface (setšoantšo sa 12) se bontša hore filimi e sa sebetseng hona joale e na le litaba tse eketsehileng tsa Cr (mohala o mofubelu) ha o bapisoa le Fe (mola o motšo) ka karolelano ea Cr: Fe> 1.0.钝化和去皱表面（图12）表明，钝化膜现在的Cr（红线) Cr（红线）含量高于Fe(黑线），Cr:Fe 比率> 1.0. Пассивированная и морщинистая поверхность (рис. 12) показывает, что пассивированная пленка теперь имеет более высокое содержания Cr, , ,,,,,,,,,,,,,,,,,,,,,,. ри соотношении Cr:Fe > 1,0. Sebaka sa passivated le sosobaneng (setšoantšo sa 12) se bontša hore filimi e fetotsoeng hona joale e na le litaba tse phahameng tsa Cr (mola o mofubelu) ho feta Fe (mola o motšo) ka tekanyo ea Cr: Fe> 1.0.
Filimi e tšesaane (< 80 Å) e fetisang chromium oxide filimi e sireletsa ho feta makholo a angstrom thick crystalline iron oxide film ho tloha motheong oa tšepe le sekala se nang le tšepe e fetang 65%.
Motsoako oa lik'hemik'hale oa sebaka sa passivated le wrinkled hona joale se bapisoa le lisebelisoa tse bentšitsoeng.Sediment boemong ba 1 ke sediment sa sehlopha sa 2 se khonang ho thehoa sebakeng;ha e ntse e bokellana, ho thehoa likaroloana tse khōloanyane tse fallang le mouoane.
Tabeng ena, kutu e bontšitsoeng e ke ke ea lebisa mefokolong e tebileng kapa ho senyeha ha boleng ba holim'a metsi.Ho sosobana ho tloaelehileng ho tla fokotsa phello e senyang holim'a metsi le ho felisa monyetla oa ho falla ho matla ha likaroloana tse ka 'nang tsa bonahala.
Setšoantšong sa 11, liphetho tsa AES li bontša hore likarolo tse teteaneng tse haufi le holim'a metsi li na le maemo a phahameng a Fe le O (500 Å of iron oxide; lemon green and blue lines, ka ho latellana), ho fetela ho maemo a mangata a Fe, Ni, Cr, le O. Fe (mohala o moputsoa) o phahame haholo ho feta oa tšepe leha e le efe, e eketseha ho tloha ho 35% holimo ho ea ho 65%.
Ka holimo, boemo ba O (mola o motala o bobebe) bo tloha ho hoo e ka bang 50% ka motsoako ho ea hoo e ka bang zero ka botenya ba filimi ea oxide e fetang 700 Å. Maemo a Ni (mola o motala o lefifi) le Cr (mohala o mofubelu) a tlase haholo holimo (<4%) mme a eketseha ho ea maemong a tloaelehileng (11% le 17%, ka ho latellana) ka botebo ba alloy. Maemo a Ni (mola o motala o lefifi) le Cr (mohala o mofubelu) a tlase haholo holimo (<4%) mme a eketseha ho ea maemong a tloaelehileng (11% le 17%, ka ho latellana) ka botebo ba alloy. Уровни Ni (темно-зеленая линия) и Cr (красная линия) чрезвычайно низки на поверхности (<4%) and увеличиваются до нормального уровня (11% песни) лава. Maemo a Ni (mola o motala o lefifi) le Cr (mohala o mofubelu) a tlaase haholo holimo (<4%) 'me a eketseha ho ea ho maemo a tloaelehileng (11% le 17% ka ho latellana) ka ho teba ka alloy.表面的Ni（深绿线）和Cr（红线）水平极低（<4%），而在合金深度处增加到正常水1到正常水1到正常水1.表面的Ni（深绿线）和Cr（红线）水平极低（<4%），而在合金深度处增加到歌常漈划1% Уровни Ni (<4%) and Cr (красная линия) на поверхности чрезвычайно низки (<4%) и увеличиваются до нормального уровня 1 % 10% haho). Maemo a Ni (mola o motala o lefifi) le Cr (mohala o mofubelu) ka holim'a metsi a tlase haholo (<4%) 'me a eketseha ho ea ho maemo a tloaelehileng a tebileng ka alloy (11% le 17% ka ho latellana).
Setšoantšo sa AES ho feiga.12 e bontša hore lera la rouge (iron oxide) le tlositsoe 'me filimi ea passivation e tsosolositsoe.Karolong e ka sehloohong ea 15 Å, boemo ba Cr (mola o mofubelu) bo phahame ho feta Fe (mola o motšo), e leng filimi e sa sebetseng.Qalong, litaba tsa Ni ka holim'a metsi e ne e le 9%, e eketseha ka 60-70 Å ka holimo ho boemo ba Cr (± 16%), ebe e eketseha ho ea boemong ba alloy ea 200 Å.
Ho qala ho 2%, boemo ba carbon (mola o moputsoa) bo theohela ho zero ho 30 Å. Boemo ba Fe qalong bo tlase (< 15%) mme hamorao bo lekana le boemo ba Cr ho 15 Å mme bo tsoela pele ho eketseha ho ea boemong ba alloy ho feta 65% ho 150 Å. Boemo ba Fe qalong bo tlase (< 15%) mme hamorao bo lekana le boemo ba Cr ho 15 Å mme bo tsoela pele ho eketseha ho ea boemong ba alloy ho feta 65% ho 150 Å. Уровень Fe вначале низкий (< 15%), позже равен уровню Cr при 15 Å и продолжает увеличиваться до уровня сплава более 65% при 15. Boemo ba Fe qalong bo tlase (< 15%), hamorao bo lekana le boemo ba Cr ho 15 Å mme bo tsoela pele ho eketseha ho feta 65% alloy level ho 150 Å. Fe 含量最初很低(< 15%)，后來在15 Å 时等于Cr 含量，并在150 Å 时继续增加到超过采65% . Fe 含量最初很低(< 15%)，后來在15 Å 时等于Cr 含量，并在150 Å 时继续增加到超过采65% . Содержание Fe изначально низкое (< 15 %), позже оно равняется содержанию Cr 15 Å и продолжает увеличиваться оно равняется содержания Litaba tsa Fe qalong li tlase (< 15%), hamorao li lekana le Cr content ho 15 Å mme li tsoela pele ho eketseha ho fihlela lihlahisoa tsa alloy li feta 65% ho 150 Å.Maemo a Cr a nyolohela ho 25% ea bokaholimo ho 30 Å mme a theohela ho 17% ka motsoako.
Boemo bo phahameng ba O haufi le bokaholimo (mola o motala o khanyang) bo fokotseha ho fihlela ho zero kamora botebo ba 120 Å.Tlhahlobo ena e bontšitse filimi e ntlafalitsoeng hantle ea holim'a lefatše.Lifoto tsa SEM litšoantšong tsa 13 le 14 li bonts'a sebopeho sa kristale se mahoashe, se mahoashe le sa porous sa bokaholimo ba 1st le 2nd iron oxide layers.Sebaka se sosobaneng se bontša phello ea kutu sebakeng se mahoashe se nang le mekoti (Lipalo 18-19).
Libaka tse sosobaneng le tse sosobaneng tse bontšitsoeng setšoantšong sa 13 le 14 ha li mamelle oxidation e matla.Lipalo 15 le 16 li bonts'a filimi e tsosolositsoeng ea passivation holim'a tšepe.